Electroless nickel plating is a widely used plating method in many industries. The usability of the coating is, however, restricted by the control problems related to the electroless nickel plating process. To ensure deposit quality, the transcendent properties of electroless nickel deposit should be accurately controlled during plating, which is challenging because of the spontaneous, unstable...

As a surface finish, electroless nickel / electroless palladium / immersion gold (ENEPIG) has received increased attention for both packaging/IC-substrate and PWB applications. With a lower gold thickness compared to conventional electroless nickel / immersion gold (ENIG) the ENEPIG finish offers the potential for higher reliability, better performance and reduced cost.[1,2] This paper shows th...

Electroless nickel is often plated on the surface of aluminum mirrors to improve the ability to polish the mirror surface. Electroless nickel plating can cause a bimetallic effect, creating distortion of a mirror surface if it is heated or cooled. Published data listing the thermal coefficient of expansion and Young’s modulus as a function of temperature for electroless nickel is not readily av...

The paper discusses optimising work on a method of processing ceramic / metal composite coatings for various applications and is based on preliminary work on processing anodes for solid oxide fuel cells (SOFCs). The composite coating is manufactured by the electroless co-deposition of nickel and yttria stabilised zirconia (YSZ) simultaneously on to a ceramic substrate. The effect on coating cha...

The information contained in this publication has been compiled from the literature and through communication with recognized experts within the metal finishing industry. It is presented as a guide to the use of electroless nickel for engineers, metallurgists, designers and others involved in materials selection. The important properties of electroless nickel deposits are described and examples...

t is well recognized that electroless I.' nickel-phosphorus offers excellent deposition characteristics, such as uniform coverage, freedom from porosity, hardness, corrosion resistance, solderability, braze and weldability, wear resistance and lubricity.' Interest in the properties of electroless nickel has grown in recent years, leading to the development of wide-ranging applications, a compre...

Two coatings have been developed for petrochemical compressor antifouling and corrosion resistance purposes. One is a multilayer composite coating with a modified polytetrafluoroethylene (PTFE) impregnated organic topcoat, which gives it superior antifouling performance to the similar coating that has been used by the compressor original equipment manufacturers (OEMs). The other is a high-phosp...

For solder based flip-chip assembly, the deposition of an under bump metallisation (UBM) layer onto the surface of the AI bondpads of the die is the first step in the wafer bumping process. The UBM is necessary, as the fragile AI pad has a tenacious oxide layer that cannot be soldered without the use of strong fluxes and a barrier layer is required to prevent dissolution of the bondpad into the...

Flip Chip (FC) Technology is gaining an increased level of importance for a variety of applications based on Flip Chip on Board or Flip Chip in Package. The first driving force for the introduction of this Technology was the need to achieve increased speed and performance along with higher I/O count. A breakthrough, however, will be the use of flip chip due to cost reduction. For this aim it is...

This paper deals with the preparation and characterization of Nickel-coated Alumina ceramic particles by Electroless Plating Technique. Nanosized α-Al2O3 powders of about 50nm in diameter are used for plating. The bath for Electroless Nickel Plating is prepared with NiCl2.6H2O, C6H5NaO7.H2O, NH4Cl and NaH2PO2.H2O. A bath temperature of 85°C, pH value of 8 and stirring time of 20 min is consider...