Mesoporous Ni–alumina catalysts (Ni–alumina-pre and Ni–alumina-post) were synthesized by one-step sol–gel method using micelle complex comprising lauric acid and nickel ion as a template with metal source and using aluminum sec-butoxide as an aluminum source. The Ni–alumina catalysts showed relatively high surface areas (303 m/g for Ni–alumina-pre and 331 m/g for Ni–alumina-post) and narrow por...

Mesoporous alumina catalysts that incorporate nickel (Ni-Alumina) with different Ni/Al molar ratios of 1:2, 1:5 and 1:10 were synthesized by a one-step sol–gel method using lauric acid as a template. The prepared Ni-Alumina catalysts showed a relatively high surface area with a narrow pore size distribution after calcination at 700 ◦C; these effects were independent of the Ni/Al molar ratio. Al...

Selecting a proper support in the catalyst system plays an important role in hydrogen production via ethanol steam reforming. In this study, sol gel made alumina supports prepared for nickel (Ni) catalysts were calcined at different temperatures. A series of (Ni/AlS.G.) catalysts were synthesized by an impregnation procedure. The influence of varying the calcination temperature of the sol gel m...

The catalytic hydrogenation of p-nitrophenol to p-aminophenol was investigated over alumina supported nickel catalysts prepared by impregnation reduction method and mechanical mixing method. The catalysts were characterized by XRD and FESEM. The results show that the nickel particle diameter of alumina supported nickel prepared by impregnation reduction method (denoted as Ni/Al2O3) is slightly ...

The comparative analysis of the electrochemical deposition of Ni and Ni-Fe nanowires (NWs) into ordered porous alumina templates is presented. The method developed allows for obtaining NWs of 50 ± 5 nm in diameter and 25 μm in length, i.e., with an aspect ratio of 500. XRD data demonstrate the polycrystalline nature of Ni and Ni-Fe in a face-centered cubic close-packed lattice. Both fabricated ...

The influence of the amount of alumina binders on the catalytic performance of Ni/HZSM-5 for hydrodeoxygenation of cyclohexanone was investigated in a fixed-bed reactor. N2 sorption, X-ray diffraction, H2-chemisorption and temperature-programmed desorption of ammonia were used to characterize the catalysts. It can be observed that the Ni/HZSM-5 catalyst bound with 30 wt.% alumina binder exhibit...

Sonochemical preparation of Co and Ni promoted MoS(2) supported on alumina was achieved by high-intensity ultrasonic irradiation of isodurene solutions containing molybdenum carbonyl, dicobalt octacarbonyl, elemental sulfur, and Al(2)O(3) or Ni-Al(2)O(3) under Ar flow. The sonochemically prepared catalysts were characterized by elemental analysis, XPS, SEM, TEM, and XEDS, and hydrodesulfurizati...

The wear resistance of Al2O3/2.5 vol.% Ni nanocomposites sintered by a conventional route was studied under ball-on-disk dry sliding conditions and compared with the same nanocomposites but consolidated by spark plasma sintering, together with alumina obtained by the same technique and by hot pressing. The results showed an improvement of about 0.5, 1 and 2 orders of magnitude, respectively. Th...

In this work the structure and chemistry of intergranular films at metal–ceramic interfaces was investigated via detailed microstructural characterization of model metal–Al2O3 nanocomposites. We report here experimental results indicating the formation and stability of equilibrium nanometer-thick films at metal–ceramic interfaces. Thin 1 nm interface films were observed for two different metal–...

An alumina-supported nickel catalyst was prepared by impregnation of Ni2+ solution onto mesoporous alumina under microwave irradiation (denoted as M-Ni/Al2O3). For comparison, a catalyst with the same nickel content was prepared by conventional impregnation method (denoted as UM-Ni/Al2O3). Both M-Ni/Al2O3 and UM-Ni/Al2O3 catalysts were applied to the syngas (H2 + CO) production by methane oxy-s...