ni-hard4 white cast iron is excellent wear resistant material and has been widely used in wearaffected equipment operated under extreme conditions, such as in mineral processing, cement, copper and iron manufacturing. in this study the effect of titanium addition (1.2, 0.7 and 0.2 wt.%) to the ni-hard 4 cast iron with the nominal composition of si= 1.5%, mn=0.5%, c=3%, p=0.05%, s= 0.05%, mo= 0....

Ni-Hard4 white cast iron is excellent wear resistant material and has been widely used in wearaffected equipment operated under extreme conditions, such as in mineral processing, cement, copper and iron manufacturing. In this study the effect of titanium addition (1.2, 0.7 and 0.2 wt.%) to the Ni-hard 4 cast iron with the nominal composition of Si= 1.5%, Mn=0.5%, C=3%, P=0.05%, S= 0.05%, Mo= 0....

Ni-Hard4 white cast iron is excellent wear resistant material and has been widely used in wearaffected equipment operated under extreme conditions, such as in mineral processing, cement, copper and iron manufacturing. In this study the effect of titanium addition (1.2, 0.7 and 0.2 wt.%) to the Ni-hard 4 cast iron with the nominal composition of Si= 1.5%, Mn=0.5%, C=3%, P=0.05%, S= 0.05%, Mo= 0....

in this research the effect of volume and morphology of eutectic carbides on tribological behaviour of ni-hard 4 cast irons have been investigated. therefore, as a result of the fact that the carbon content effects the carbides morphology of ni-hard cast irons, the chemical compositions of five different specimens were kept constant with the exception of the carbon content, which was varied fro...

In this research the effect of volume and morphology of eutectic carbides on tribological behaviour of Ni-Hard 4 cast irons have been investigated. Therefore, as a result of the fact that the carbon content effects the carbides morphology of Ni-hard cast irons, the chemical compositions of five different specimens were kept constant with the exception of the carbon content, which was varied fro...

In this research the effect of volume and morphology of eutectic carbides on tribological behaviour of Ni-Hard 4 cast irons have been investigated. Therefore, as a result of the fact that the carbon content effects the carbides morphology of Ni-hard cast irons, the chemical compositions of five different specimens were kept constant with the exception of the carbon content, which was varied fro...

From the standpoint of processing, hard chromium layer plate may be applied to steels, cast iron, aluminum and nickel base alloys. Cast iron can be plated provided that the surface is capable of conducting the required current and is reasonably free of voids, pits, gross silicate inclusions, and massive segregation. There are many difficulties arising from graphite phase and deposition of hydro...