the nanocrystallization of co67fe4cr7si8b14 amorphous ribbons which prepared by planar flow melt spinning process (pfms) was investigated. crystallization of the ribbons was studied by differential thermal analysis (dta), x-ray diffraction (xrd) and transmission electron microscopy (tem). the dta result of amorphous ribbon at heating rate of 10˚c/min showedoccurrence of phase transitions in two...

In this work, we have studied the influence of dc joule-heating thermal processing on the structure, magnetoimpedance (MI) and thermal properties of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1, and 2) rapidly solidified melt-spun ribbons. The nanocrystallization process was carried out by the current annealing of as-spun samples at various current densities. As-spun and joule-heated samples were studied...

The P content dependencies of the nanocrystallization behaviors and high temperature magnetic properties of the Fe 54.6 Co 29.4 Si 2.8 (B 0.8ÀY P Y) 14 Nb 1 Cu 1 (Y ¼ 0, 0.2, and 0.3) alloys have been investigated. Alloys were prepared by melt spinning and subsequently annealed in an argon atmosphere to induce nanocrystallization. P addition increases primary crystallization temperature (Tx 1),...

The nanocrystallization of Co67Fe4Cr7Si8B14 amorphous ribbons which prepared by planar flow melt spinning process (PFMS) was investigated. Crystallization of the ribbons was studied by differential thermal analysis (DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The DTA result of amorphous ribbon at heating rate of 10˚C/min showedoccurrence of phase transitions in two...

Multicomponent Fe65.5Cr4Mo4Ga4P12C5B5.5 amorphous alloy is known to have good soft magnetic properties combined with large glass-forming ability. Searching for a nanocrystalline structure that could improve its magnetic properties, Cr and Mo were partially substituted by Cu. The devitrification process of Cu-containing alloys shows an additional broad crystallization event that can be described...

In recent years, a lot of research has been done in the field of producing soft magnetic nano composites by means of mechanical alloying. These materials indicate more electrical resistance and permeability in comparison with soft magnetic composites (SMCs). In this research, reduction of silicothermal mixed powder (Nickel-oxide, Silicon and Iron) was carried out by mechanical alloying to form ...

In this work, nanocrystalline Fe85Si10Ni5 soft magnetic powders were prepared by mechanical alloying and subsequent annealing to reduce the internal stresses and lattice strains. The powders were mixed with phenolic resin and warm pressed to produce nanostructured soft magnetic composites. The effect of annealing time and temperature on the crystalline structure, microstructure and magnetic pro...