Red pine leafs were applied for the green method preparation of MgO nano-plates. The MgO nano-plates were used for the one-pot synthesis of dihydropyrano [3,2-c] chromene derivatives. This procedure is very simple and affords excellent yields. MgO nanoplates were synthesized via a simple precipitation method with the using of an extract solution of red pine leaves. The XRD pattern shows a cubic...

Red pine leafs were applied for the green method preparation of MgO nano-plates. The MgO nano-plates were used for the one-pot synthesis of dihydropyrano [3,2-c] chromene derivatives. This procedure is very simple and affords excellent yields. MgO nanoplates were synthesized via a simple precipitation method with the using of an extract solution of red pine leaves. The XRD pattern shows a cubic...

Nano MgO has been synthesized by hydration and dehydration method by modifies the commercial MgO. The prepared MgO had been investigated as a heterogeneous base catalyst for transesterification process for biodiesel production using palm oil. TGA, FT-IR and XRD results obtained from this study lie each other and proved in the formation of nano MgO from decomposition of Mg(OH)2. This study prove...

MgO is an important inorganic material, which can be used in many aspects, such as catalyst, toxic-waste remediation agent, adsorbent, and others. In order to make use of MgO, nano-MgO was prepared by ultrasonic method using Mg (CH3COO)2.2H2O as precursor, NaOH aqueous solution as precipitant in this paper. Effect factors on MgO nano-particle size were investigated. Characteristics of samples w...

dehydration method by modifies the commercial MgO. The prepared MgO had been investigated as a heterogeneous base catalyst for transesterification process for biodiesel production using palm oil. TGA, FT-IR and XRD results obtained from this study lie each other and proved in the formation of nano MgO from decomposition of Mg(OH) 2. This study proved that the prepared nano MgO was a better base...

Nano-MgO was successfully deposited on titania using deposition-precipitation method. The catalyst produced was characterised using FTIR, XRD, BET and XRF and its activity was tested on the transesterification reaction of soybean oil to biodiesel. The catalyst activity improved when the reaction temperature was increasedfrom 150 and 225 C. It was also observed that increasing the reaction time ...

nanocrystalline magnesium oxides were prepared by sol–gel method and were characterized by x-ray diffraction, n2-bet, sem and infrared spectroscopy techniques. the results confirmed the formation of nano- mgo materials with crystallite size in range of 5-20 nm and surface areas of 336-556m2/g. the product has been tested as destructive adsorbent for the decontamination of (2-chloroethyl) ethyl ...

The surface-enhanced Raman spectroscopy (SERS) technique is of great importance for insight into the transient reaction intermediates and mechanistic pathways involved in heterogeneously catalyzed chemical reactions under actual reaction conditions, especially in water. Herein, we demonstrate a facile method for in situ synthesis of nanocrystalline magnesium oxide-Ag(0) (nano MgO-Ag(0)) hybrid ...

BACKGROUND Fossil fuels' pollution and their non-renewability have motivated the search for alternative fuels. Some common example of seed oils are sunflower oil, date seed oil, soy bean oil. For instance, soy methyl and soy-based biodiesel are the main biodiesel. Biodiesel is a clean diesel fuel that can be produced through transesterification reaction. Recycled cooking oil, on the other hand,...

a facile and simple method was proposed to control the size and shape of the mgo nano structures with high surface area in the presence of efficient and cheap templates like peg 200, peg 600, peg 4000 and sorbitol at low temperature within a little time. nano rods and nanoparticles have been achieved by applying these templates and altering other growth parameters. the products were characteriz...