X-ray diffraction showed that an La7.0Mg75.5Ni17.5 alloy prepared via inductive melting was composed of an La2Mg17 phase, an LaMg2Ni phase, and an Mg2Ni phase. After the first hydrogen absorption/desorption process, the phases of the alloy turned into an La–H phase, an Mg phase, and an Mg2Ni phase. The enthalpy and entropy derived from the van’t Hoff equation for hydriding were −42.30 kJ·mol−1 ...

mechanical alloying of binary and ternary elemental powder mixtures with the nominal compositions of mg2ni and mg(2-x)mnxni (x= 0, 0.05, 0.10 and 0.15 at. %) were carried out in a planetary ball mill for various milling times of 5, 10, 15, 20, 30 and 60 h. x-ray diffraction and field emission scanning and transmission electron microscopy were used for the characterization of the milled products...

Mg2NiH4 thin films have been prepared by activated reactive evaporation in a molecular beam epitaxy system equipped with an atomic hydrogen source. The optical reflection spectra and the resistivity of the films are measured in situ during deposition. In situ grown Mg2NiH4 appears to be stable in vacuum due to the fact that the dehydrogenation of the Mg2NiH4 phase is kinetically blocked. Hydrog...

Mechanical alloying of binary and ternary elemental powder mixtures with the nominal compositions of Mg2Ni and Mg(2-x)MnxNi (x= 0, 0.05, 0.10 and 0.15 at. %) were carried out in a planetary ball mill for various milling times of 5, 10, 15, 20, 30 and 60 h. X-ray diffraction and field emission scanning and transmission electron microscopy were used for the characterization of the milled products...

© 2012 Zhang et al., licensee InTech. This is an open access chapter distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/3.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. The Preparation and Hydrogen Storage Performances of Nanocrystalline and Amorphous Mg2...

Abstract: Mg2Ni alloy and Mg2Ni–x wt% TiO2 (x = 3, 5 and 10 wt %) composites are prepared by mechanical alloying. The produced alloy and composites are characterized as the particles with nanocrystalline/amorphous structure. The effects of TiO2 on hydrogen storage properties are investigated using anodic polarization and electrochemical impedance spectroscopy. It is demonstrated that the initia...

Liquid metal dealloying (LMD) has recently attracted significant attention. Because the LMD process enables production of three-dimensional (3D) interconnected non-noble metallic materials. In addition, melt medium is useful for development heterostructure (HS) metal–metal composites. However, solidified liquid phase (low melting point metals such as Mg, Bi, Sn, or Cu) a much lower strength tha...