in this work, we investigated synthesis, magnetic properties of silica coated metal ferrite, (cofe2o4)/sio2 and manganese doped cobalt ferrite nanoparticles (mnxco1-xfe2o4 with x= 0.02, 0.04 and 0.06)/sio2 for possible biomedical application. all the ferrites nanoparticles were prepared by co-precipitation method using fecl3.6h2o, cocl2.6h2o and mncl2.2h2o as precursors, and were silica coated ...

In the present study, magnetic core-shell manganese ferrite nanoparticles (MCMNP) were synthesized and used for construction of a magnetic core-shell manganese ferrite nanoparticles modified screen-printed carbon electrode (MCSNP-SPCE). Cyclic voltammetry was used to study the electrochemical behavior of chlorpromazine (CPZ) and its determination was conducted by applying square wave voltammetr...

The optical properties of multi-functionalized cobalt ferrite (CoFe2O4), cobalt zinc ferrite (Co0.5Zn0.5Fe2O4), and zinc ferrite (ZnFe2O4) nanoparticles have been enhanced by coating them with silica shell using a modified Stöber method. The ferrites nanoparticles were prepared by a modified citrate gel technique. These core/shell ferrites nanoparticles have been fired at temperatures: 400°C, 6...

We report a novel core-shell-structured ternary nanocube of MnZn ferrite synthesized by controlling the reaction temperature and composition in the absence of conventionally used reducing agents. The highly monodispersed core-shell structure consists of an Fe(3)O(4) core and an MnZn Ferrite shell. The observation of a Moiré pattern indicates that the core and the shell are two highly crystallin...

The atomic level structure of a series of monodisperse single crystalline nanoparticles with a magnetic core of manganese ferrite was studied using X-ray absorption fine structure (EXAFS) and X-ray absorption near edge structure (XANES) techniques at both the Fe and Mn K-edges, and conventional and high resolution transmission electron microscopy (TEM and HRTEM). In particular, insights on the ...

Two sets of core/shell magnetic nanoparticles, CoFe2O4/Fe3O4 and Fe3O4/CoFe2O4, with a fixed diameter of the core (~ 4.1 and ~ 6.3 nm for the former and latter sets, respectively) and thickness of shells up to 2.5 nm were synthesized from metal chlorides in a diethylene glycol solution. The nanoparticles were characterized by X-ray diffraction, transmission electron microscopy, and magnetic mea...

Bimagnetic monodisperse CoFe₂O₄/Fe₃O₄ core/shell nanoparticles have been prepared by solution evaporation route. To demonstrate preferential coating of iron oxide onto the surface of ferrite nanoparticles X-ray diffraction (XRD), High resolution transmission electron microscope (HR-TEM) and Raman spectroscopy have been performed. XRD analysis using Rietveld refinement technique confirms single ...

In this work, we investigated synthesis, magnetic properties of silica coated metal ferrite, (CoFe2O4)/SiO2 and Manganese doped cobalt ferrite nanoparticles (MnxCo1-xFe2O4 with x= 0.02, 0.04 and 0.06)/SiO2 for possible biomedical application. All the ferrites nanoparticles were prepared by co-precipitation method using FeCl3.6H2O, CoCl2.6H2O and MnCl2.2H2O as precursors, and were silica coated ...

In this work, we investigated synthesis, magnetic properties of silica coated metal ferrite, (CoFe2O4)/SiO2 and Manganese doped cobalt ferrite nanoparticles (MnxCo1-xFe2O4 with x= 0.02, 0.04 and 0.06)/SiO2 for possible biomedical application. All the ferrites nanoparticles were prepared by co-precipitation method using FeCl3.6H2O, CoCl2.6H2O and MnCl2.2H2O as precursors, and were silica coated ...