Hydrophobicity properties of graphite and green synthesized graphene (gsG) from exfoliated graphite/GO towards polymer membrane characteristic and properties at different weight percentage concentrations (1, 2, 3, 4 and 5 wt. %) were investigated. PSf/graphite and PSf/gsG membranes were characterized in term of hydrophobicity, surface bonding, surface roughness and porosity. FTIR peaks revealed...

In this work, the reduced graphene nanosheets were synthesized from pre-exfoliated graphite flakes. The pristine graphite flakes were firstly pre-exfoliated to graphite nanoplatelets in the presence of acetic acid. The obtained graphite nanoplatelets were treated by Hummer’s method to produce graphite oxide sheets and were finally exfoliated to graphene nanosheets by ultrasonication and reducti...

Exfoliated graphite electrodes have been used to detect uric acid at neutral pHs, by following its oxidation. A linear range of 5 ± 53 M and a detection limit of 5 M are observed at a pH of 7.0. Uric acid was found to be selectively adsorbed on exfoliated graphite surface in the presence of excess ascorbic acid. This leads to its selective determination in the presence of ascorbic acid. Simulta...

We report a simple yet versatile method to simultaneously achieve the exfoliation and reduction of graphite oxide. By treating graphite oxide powders in a commercial microwave oven, reduced graphite oxide materials could be readily obtained within 1 min. Extensive characterizations showed that the as-prepared materials consisted of crumpled, few-layer thick and electronically conductive graphit...

Here we demonstrate a controlled two-step partial exfoliation method to synthesize functionalized exfoliated graphite substrates. Ultrathin and functionalized graphene sheets anchoring on the graphite provide a large conductive surface area for loading pseudo-capacitive MnO2 nanosheets. The functionalized exfoliated graphite/MnO2 electrode achieved an excellent areal capacitance of 244 mF cm(-2...

Exfoliated graphite (obtained by rapid heating of sulfuric-acid intercalated and subsequently deacidified graphite flakes) is optionally subjected to residual acidity removal, which involves repeated washing with water, such that the pH of the wash water increases from 2 to 7. Compared to washed exfoliated graphite, the unwashed material exhibits lower specific surface area (24 vs. 45 m/g), a h...

Few-layer graphene has been prepared by electrochemical intercalation of graphite cathode using Na/ dimethyl sulfoxide complexes as intercalation agent. By adding thionin acetate salt into the electrolyte, the exfoliated graphite is stabilized and further exfoliated into few-layer graphene. Raman and X-ray photoelectron spectra indicate that the graphene material has lower content of defects an...

Large-flake graphene membranes up to 300 microm(2) can be exfoliated from graphite by oleyl amine based on solvothermal conditions. The exfoliated graphene sheets are of high quality and have few defects. The graphene dispersion, predominantly composed of monolayer graphene, had a high concentration of 0.15 mg ml(-1), and can be stabilized against re-aggregation.

Exfoliated graphite (EG) refers to graphite that has a degree of separation of a substantial portion of the carbon layers in the graphite. Graphite nanoplatelet (GNP) is commonly prepared by mechanical agitation of EG. The EG exhibits clinginess, due to its cellular structure, but GNP does not. The clinginess allows the formation of EG compacts and flexible graphite sheet without a binder. The ...