The material flow and microstructural evolution in the friction stir welds of a 6061-Al alloy to itself and of a 6061-Al alloy to 2024-Al alloy plates of 12.7 mm in thickness were studied under different welding conditions. The results showed that plastic deformation, flow, and mechanical mixing of the material exhibit distinct asymmetry characteristics at both sides of the same and dissimilar ...

The most effective method to reduce CO2 gas emission from the steam power plant is to improve its performance by elevating the steam temperature to more than 700 ◦C. For this, it is necessary to develop applicable materials at high temperatures. Ni-based Alloy 617 and 12Cr steel are used in steam power plants, due to their remarkable mechanical properties, high corrosion resistance, and creep s...

the microstructure of hp stainless steel in aged and aged + solution annealed conditions and solutionized alloy 800 was characterized by optical microscopy, scanning electron microscopy (sem), and transmission electron microscopy (tem) equipped by eds. all phases present in the above condition were described. the effects of solution annealing heat treatment temperature on the microstructure, te...

in the present study, the corrosion behavior of aisi 347 austenitic stainless steel to astm a335 low alloysteel dissimilar joint was investigated. for this purpose, two filler metals, er309l and ernicr-3, were selected to be used during the gas tungsten arc welding process. to investigate the corrosion behavior of the joints after welding, the specimens were tested in 3.5% sodium chloride solut...

The effects of metal combinations on cytotoxicity were examined following dynamic extraction by freely gyrating two spherical metals in a glass vessel. The cell viabilities of an Au alloy, a Ag-Pd-Au alloy and Ti were little affected by combinations among three metals. Cell viability ranged between 60 and 80% when precious alloys were in combination with Co-Cr or Ni-Cr alloys. Ti showed a clear...

in the present study, the microstructure and mechanical properties of the dissimilar welding betweenastm a335 low alloy steel and er309l austenitic stainless steel were investigated using the gastungsten arc welding process. the welding of dissimilar materials between astm a335 low alloy steeland er309l austenitic stainless steel was found to have a significant effect on the microstructure when...

In the present study, the microstructure and mechanical properties of the dissimilar welding between ASTM A335 low alloy steel and ER309L austenitic stainless steel were investigated using the gas tungsten arc welding process. The welding of dissimilar materials between ASTM A335 low alloy steel and ER309L austenitic stainless steel was found to have a significant effect on the microstructure w...

In the present study, the Weldability and microstructure of dissimilar welds of AISI 347austenitic stainless steel to ASTM A335 low alloy steel was investigated. For this purpose, gas tungsten arc welding process and two filler metals including ERNICr-3 and ER309L were used. After welding, the microstructure of the different zones of each joint, including weld metals, heat affected zone (HAZ) 1...

Titanium alloy TC1 and Aluminum alloy LF6 were butt jointed and lap jointed by friction stir welding (FSW), and the influence of process parameters on formation of weld surface, cross-section morphology and strength were studied. The results show that, Titanium and Aluminum dissimilar alloy is difficult to be butt joined by FSW, and some defects such as cracks and grooves are easy to occur. Whe...

In this work, the dissimilar joint of AA7003-T4 and 6060-T4 alloy has been produced by friction stir welding (FSW). The microstructure was examined by optical microscope (OM), electron back scattered diffraction (EBSD), transmission electron microscopy (TEM), and the mechanical properties of the joint were investigated. It is demonstrated that sound dissimilar joint can be produced through FSW....