A simple theoretical model based on electric-field-assisted growth and dissolution of the barrier oxide has been proposed to understand the mechanisms for formation of a one-dimensional 1D anodic aluminum oxide AAO nanopore array. It is shown that formation of a one-dimensional horizontal nanopore array is the natural result of the self-adjusting effect of anodic oxidation. Because the electric...

This paper presents the development of low cost Nano membrane fabrication system. The system is specially designed for anodic aluminum oxide membrane. This system is capable to perform the processes such as anodization and electro-polishing. The designed machine was successfully tested for ‘mild anodization’ (MA) for 48 hours and ‘hard anodization’ (HA) for 3 hours at constant 0C. The system is...

Porous alumina film on aluminum with gel-like pore wall was prepared by a two-step anodization of aluminum, and the corresponding gel-like porous film was etched in diluted NaOH solution to produce alumina nanowires in the form of densely packed alignment. The resultant alumina nanowires were reacted with NH(3) and evaporated aluminum at an elevated temperature to be converted into densely pack...

This article is an introduction to anodization of aluminum, which is a subject of electrochemistry. Anodization of aluminum under a controlled electrochemical condition yields ordered porous alumina with a close-packed hexagonal array of cylindrical nanochannels. The diameter, density, and aspect ratio of pores can be tightly controlled by varying the anodization condition, which makes the poro...

Voltage controlled wavelength tuning of the localized surface plasmon resonance of gold nanoparticles on an aluminum film is demonstrated in single particle microscopy and spectroscopy measurements. Anodization of the Al film after nanoparticle deposition forms an aluminum oxide spacer layer between the gold particles and the Al film, modifying the particle-substrate interaction. Darkfield micr...

The history of electrochemical oxidation of aluminum dates back to the beginning of the last century. Anodic treatment of aluminum were intensively investigated to obtain protective and decorative films on its surface [1]. More recently, applications of porous alumina with a huge surface area and a relatively narrow pore size distribution have been exploited [2]. For example, several attempts t...

Nanochannel arrays were fabricated by the self-organized multi-electrolyte-step anodic aluminum oxide [AAO] method in this study. The anodization conditions used in the multi-electrolyte-step AAO method included a phosphoric acid solution as the electrolyte and an applied high voltage. There was a change in the phosphoric acid by the oxalic acid solution as the electrolyte and the applied low v...

Anodizing is an electrochemical process that converts the metal surface into a decorative, durable, corrosion-resistant, anodic oxide finish. Aluminum is ideally suited to anodizing, although other nonferrous metals, such as magnesium and titanium, also can be anodized. The anodic oxide structure originates from the aluminum substrate and is composed entirely of aluminum oxide. This aluminum ox...

Anodizing is an electrochemical process that converts the metal surface into a decorative, durable, corrosion-resistant, anodic oxide finish. Aluminum is ideally suited to anodizing, although other nonferrous metals, such as magnesium and titanium, also can be anodized. The anodic oxide structure originates from the aluminum substrate and is composed entirely of aluminum oxide. This aluminum ox...

Focused ion beam lithography and a two-step anodization have been combined to fabricate a vertical fan-out platform containing an array of unique probes. Each probe comprises three anodic alumina nanochannels with a fan-out arrangement. The lithography is used to pattern an aluminum sheet with a custom-designed array of triangular 'cells' whose apexes are composed of nanoholes. The nanoholes gr...