Type transformation in CuInSe2 and CuInS2 solar cells is an important issue with far reaching consequences. In the present study, the presence of a p-n homojunction inside CuInS2 in a TiO2/CuInS2 device is revealed with a detailed impedance spectroscopy and capacitance study. A n-type CuInS2 film with a thickness of 40 nm is found at the TiO2 n-type /CuInS2 p-type interface. The effective donor...

Bright and stable CuInS2/ZnS@SiO2 nanoparticles with near-infrared (NIR) emission were competently prepared by incorporating the as-prepared hydrophobic CuInS2/ZnS quantum dots (QDs) directly into lipophilic silane micelles and subsequently an exterior silica shell was formed. The obtained CuInS2/ZnS@SiO2 nanoparticles homogeneously comprised both single-core and multicore remarkable CuInS2/ZnS...

Photoinduced interfacial charge carrier generation, separation, trapping, and recombination in TiO2 In2S3 CuInS2 cells have been studied with time-resolved microwave conductivity TRMC . Single layer, double layer, and complete triple layer configurations have been studied. Selective electronic excitation in one of the components is accomplished by using monochromatic pulsed laser excitation. In...

A novel, rapid and highly sensitive fluorescence turn-on assay for the detection of biothiols (glutathione, and L-cysteine), histidine and threonine was developed. Water-soluble CuInS2 ternary quantum dots (QDs) capped by mercaptopropionic acid (MPA) were directly synthesized in aqueous solution, and then functionalized using tyrosine molecules to form tyrosine-functionalized CuInS2 QDs (T-CuIn...

This paper presents a facile solvothermal method of synthesizing copper indium sulfide (CuInS2) quantum dots (QDs) via a non-coordinated system using polyetheramine as a solvent. The structural and optical properties of the resulting CuInS2 QDs were investigated using composition analysis, absorption spectroscopy, and emission spectroscopy. We employed molar ratios of I, III, and VI group eleme...

Wurtzite CuInS2 nanoleaves were synthesized by Cu1.94S-assisted growth. By observing the evolution of structures and phases during the growth process, Cu1.94S nanocrystals were found to be formed after uninterrupted oxidation and sulfidation of copper nanoparticles at the early stage, serving as catalysts to introduce the Cu and In species into CuInS2 nanoleaves growth for inherent property of ...

The possibility of doping and Fermi Level pinning of CuInS2 thin layer solar cell absorbers caused by the diffusion of Cd into the absorber during junction formation via chemical bath deposition was investigated. The analysis of thin CdS layers deposited on CuInS2 showed the amount of deposition-induced band bending on the CuInS2 surface (position of the Fermi Level in the respective band gaps)...

In this work, the solution-processed CH3NH3PbI3 perovskite/copper indium disulfide (CuInS2) planar heterojunction solar cells with Al2O3 as a scaffold were fabricated at a temperature as low as 250°C for the first time, in which the indium tin oxide (ITO)-coated glass instead of the fluorine-doped tin oxide (FTO)-coated glass was used as the light-incidence electrode and the solution-processed ...

2014 Novel methods for the material synthesis, crystal growth and film preparation of CuInS2 were developed, some of their properties were characterized. CuInS2 single crystals were grown by iodine vapour transport. The habit-planes were determined to be (112) and (110). The lattice parameters were determined to be a = 5.517 Å, c = 11.122 Å (tetragonal). The as-grown crystals were n-type with r...

In the present work, CuInS2 nanoparticles have been successfully synthesized by water-bath method with deionized water as solvent and thioglycolic acid as complexing agent at 80°C. The phase transition of CuInS2 from chalcopyrite to wurtzite was realized by adjusting the pH value of reaction solution. The emergence of Cu2S in the condition of higher pH value of reaction solution led to the form...