in this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. simulation results showed that mode i was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. afterward, the fract...

As fretting fatigue cracks are initiated at an early stage of life, the fretting fracture process is dominated by the stable growth of cracks. Hence the measurement of crack length is very important. This paper demonstrates the suitability of the DC potential drop technique for the measurement of fretting cracks. A calibration has been established for monitoring crack growth in BS L65 copper al...

In this study, the pitting type of corrosion growth characteristics, fatigue crack initiation and propagation behavior; axial fatigue tests were carried out on precipitation hardened martensitic Custom 450 steel in the air and 3.5wt% NaCl solution. Using the ratio of the depth to the half-width of the pits; (a/c)= 1.5±0.2 the corrosion pit depth growth law was obtained as a function of stress a...

Fretting nucleation models and three-dimensional finite element analyses are used to compute the fretting fatigue life for metallic components. The models predict crack nucleation cycles and location(s). Discrete crack growth simulations provide stress intensity factor histories, with multiple, non-planar, three-dimensional cracks possible. The histories are input into crack growth rate model(s...

In the short crack regime of the fatigue process, grain boundaries in steels are barriers against crack growth. In this paper, we use: (1) a method involving crack density; and (2) a method of dimensional analysis, to evaluate the effects of grain size and grain-boundary resistance on short crack behaviour and fatigue life. The results show that the fatigue life increases with a decrease in gra...

During the design stage, realistic life time predictions for components help to reduce test cycles and allow for an optimization with respect to both production and repair costs (see e.g. Schuëller et al. 1996). Accurate predictions of the mean life time and its standard deviation can be obtained from a fracture mechanics approach that takes the uncertainties in the material parameters into acc...

Ultrasonic methods have been implemented for in situ sizing of fatigue cracks near fastener holes. These techniques, however, only provide an estimate at the time of the measurement and cannot predict the remaining life of the structure. In contrast, statistical crack propagation approaches model the expected fatigue life based on worst-case fatigue process assumptions. The authors have recentl...

In this paper, the stress intensity factor (SIF) variations along an arbitrarily developing crack front, the non-planar fatigue-crack growth patterns, and the fatigue life of a round bar with an initially straight-fronted surface crack, are studied by employing the 3D symmetric Galerkin boundary element method-finite element method (SGBEM-FEM) alternating method. Different loading cases, involv...

There is an increasing need to assess the service life of components containing defect which operate at high temperature. This paper describes the current fracture mechanics concepts that are employed to predict cracking of engineering materials at high temperatures under static and cyclic loading. The relationship between these concepts and those of high temperature life assessment methods is ...