Corrosion of 1020 carbon steel coupons in natural seawater over a 1-year period was more aggressive under strictly anaerobic stagnant conditions than under aerobic stagnant conditions as measured by weight loss and instantaneous corrosion rate (polarization resistance). Under oxygenated conditions, a two-tiered oxide layer of lepidocrocite/goethite formed. The inner layer was extremely tenaciou...

The corrosion of Ag in an atmosphere of ozone and humidity with or without irradiation by ultraviolet (UV) light was investigated. A modified coulometric reduction technique was used, substituting sulphate solution for chloride solution, to prevent the spontaneous transformation of silver oxide corrosion product to chloride in the reduction solution. The presence of both ozone and UV radiation ...

The relationship between dissolved oxygen (DO) and corrosion behavior of X80 steel in acidic soil simulated solution was studied by potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS), scanning Kelvin probe technique (SKP) and X-ray diffraction (XRD). Results showed that the presence of DO accelerated the cathodic process of corrosion for X80 steel in the acidic so...

Since many household systems are fabricated out of metallic materials, changes to the household environment that accelerate corrosion rates will increase the frequency of failures in these systems. Recently, it has been reported that homes constructed with imported wallboard have increased failure rates in appliances, air conditioner heat exchanger coils, and visible corrosion on electrical wir...

Blistering, delamination, substrate deterioration Blistering, delamination, corrosion Blistering, reduced cohesion, film splitting, delamination Blistering, reduced cohesion, delamination, corrosion Blistering, intercoat delamination From components of paint film (e.g., inhibitive pigments, solvents, additives, etc.) From components of lower paint films (e.g., inhibitive pigments, solvents, add...

A mechanistic model was developed for predicting carbon dioxide corrosion rates of carbon steel pipes in multiphase flow conditions. The model incorporates the chemistry, thermodynamics of carbon dioxide dissolution, multiphase mass transfer, electrochemical kinetics on the metal surface and the presence of a corrosion product film. The predicted corrosion rates show good agreement with the exp...

The effect of oil soluble commercial corrosion inhibitors (OSCI) on the growth of bacteria and its corrosion inhibition efficiency were investigated. Corrosion inhibition efficiency was studied by rotating cage test and the nature of biodegradation of corrosion inhibitor was also analyzed by using FTIR, NMR and GC-MS. This isolate has the capacity to degrade the aromatic and aliphatic hydrocarb...

Finite element analyses were conducted to clarify the role of corrosion product films (CPFs) in stress corrosion cracking (SCC). Flat and U-shaped edge-notched specimens were investigated in terms of the CPF-induced stress in the metallic substrate and the stress in the CPF. For a U-shaped edge-notched specimen, the stress field in front of the notch tip is affected by the Young's modulus of th...

About a century ago, researchers first recognized a connection between the activity of environmental microorganisms and cases of anaerobic iron corrosion. Since then, such microbially influenced corrosion (MIC) has gained prominence and its technical and economic implications are now widely recognized. Under anoxic conditions (e.g., in oil and gas pipelines), sulfate-reducing bacteria (SRB) are...