cofecu nanowires were deposited by pulsed electrodeposition technique into the porous alumina templates by a two-step mild anodization technique, using the single-bath method. the electrodeposition was performed in a constant electrolyte while cu constant was controlled by electrodeposition current. the electrodeposition current was 3.5, 4.25, 5 and 6 ma. the effect of electrodeposition current...

CoFeCu nanowires were deposited by pulsed electrodeposition technique into the porous alumina templates by a two-step mild anodization technique, using the single-bath method. The electrodeposition was performed in a constant electrolyte while Cu constant was controlled by electrodeposition current. The electrodeposition current was 3.5, 4.25, 5 and 6 mA. The effect of electrodeposition current...

The Fe nanowires were prepared by Ac electrodeposition method. The two steps anodized aluminum oxides (alumina) were used as templates for electrodeposition of magnetic nanowires. Sulfuric acid was used to anodize aluminum. The pours diameter and growth rate of alumina were investigated. The FeSO4 electrolyte was used for growth of nanowires. The prepared magnetic nanowires were characterized b...

cofe/cu multilayer nanowires were electrodeposited into anodic aluminum oxide templates prepared by a two-step mild anodization method, using the single-bath technique. nanowires with 30 nm diameter and the definite lengths were obtained. the effect of cofe layers thickness and annealing on the magnetic behavior of the multilayer nanowires was investigated. the layers thickness was controlled t...

The effect of length variation on the magnetic properties of NiFe alloy nanowires electrodeposited into the alumina template was investigated. The diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. Energy dispersive spectroscopy results showed Ni3Fe7 composition of the alloy nanowire...

NiCu alloy nanowires arrays were embedded into the anodic aluminum oxide (AAO) template by ac-pulse electrodeposition. Different off-time were used in electrolyte with constant concentration of Ni and Cu and acidity of 3. The effect of deposition parameters on alloy contents was investigated by studying the microstructure and magnetic properties of as-deposited NiCu alloy nanowires. Atomic forc...

the effect of length variation on the magnetic properties of nife alloy nanowires electrodeposited into the alumina template was investigated. the diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. energy dispersive spectroscopy results showed ni3fe7 composition of the alloy nanowires.  the magnetic prope...

nicu alloy nanowires arrays were embedded into the anodic aluminum oxide (aao) template by ac-pulse electrodeposition. different off-time were used in electrolyte with constant concentration of ni and cu and acidity of 3. the effect of deposition parameters on alloy contents was investigated by studying the microstructure and magnetic properties of as-deposited nicu alloy nanowires. atomic forc...

CoFe/Cu multilayer nanowires were electrodeposited into anodic aluminum oxide templates prepared by a two-step mild anodization method, using the single-bath technique. Nanowires with 30 nm diameter and the definite lengths were obtained. The effect of CoFe layers thickness and annealing on the magnetic behavior of the multilayer nanowires was investigated. The layers thickness was controlled t...

coni nanowires were deposited by pulsed electrodeposition technique into porous alumina templates. the effect of off time between pulses (toff) and reductive/oxidative time (treduc/oxid) on the microstructure and magnetic properties of the coni nanowires were investigated. maximum coercivity and squareness were obtained for samples fabricated at treduc/oxid= 0.5 ms and toff =400 ms. the coerciv...