Oil-chitosan composite spheres were synthesized by encapsulation of sunflower seed oil in chitosan droplets, dropping into NaOH solution and in situ solidification. Hydrophilic materials (i.e., iron oxide nanoparticles) and lipophilic materials (i.e., rhodamine B or epirubicin) could be encapsulated simultaneously in the spheres in a one step process. The diameters of the prepared spheres were ...

The production and use of iron oxide nanoparticles are growing exponentially due to its wide applications in different fields of science and technology. The objective of this study is to synthesize iron oxide nanoparticles, and modification of its surface to make it less toxic. The iron oxide nanoparticles were synthesized by chemical co-precipitation method, and surface modification was done u...

Silane modified iron (III) oxide (SiFe2O3) nanoparticles reinforced chitosan (CS) nanocomposite membranes were prepared by solcast transformation method. The iron (III) oxide nanoparticles and nanocomposite membranes were investigated by UV (Visible) spectroscopy, FT-IR spectroscopy, XRD, SEM and TEM. The size and shape of iron (III) oxide and Si-Fe2O3 nanoparticles were determined by XRD and T...

BACKGROUND Bone disorders (including osteoporosis, loosening of a prosthesis, and bone infections) are of great concern to the medical community and are difficult to cure. Therapies are available to treat such diseases, but all have drawbacks and are not specifically targeted to the site of disease. Chitosan is widely used in the biomedical community, including for orthopedic applications. The ...

Iron oxide nanoparticles (INPs) have potential biological, biomedical and environmental applications. These applications require surface modification of the iron oxide nanoparticles, which makes it non-toxic, biocompatible, stable and non-agglomerative in natural and biological surroundings. In the present study, iron oxide nanoparticles (INPs) and chitosan oligosaccharide coated iron oxide nan...

BACKGROUND AND METHODS Magnetic iron oxide nanoparticles were prepared using a sonochemical method under atmospheric conditions at a Fe²⁺ to Fe³⁺ molar ratio of 1:2. The iron oxide nanoparticles were subsequently coated with chitosan and gallic acid to produce a core-shell structure. RESULTS X-ray diffraction demonstrated that the magnetic nanoparticles were pure Fe₃O₄ with a cubic inverse sp...

Staphylococcus aureus can adhere to most foreign materials and form biofilm on the surface of medical devices. Biofilm infections are difficult to resolve. The goal of this in vitro study was to explore the use of chitosan-coated nanoparticles to prevent biofilm formation. For this purpose, S. aureus was seeded in 96-well plates to incubate with chitosan-coated iron oxide nanoparticles in order...

Macroporous chitosan spheres encapsulating superparamagnetic iron oxide nanoparticles were synthesized by a facile and effective one-step fabrication process. Ferro-gels containing ferrous cations, ferric cations and chitosan were dropped into a sodium hydroxide solution through a syringe pump. In addition, a sodium hydroxide solution was employed for both gelation (chitosan) and co-precipitati...

We have developed novel Pluronic/chitosan nanocapsules encapsulating iron oxide nanoparticles. These nanocapsules were produced by dispersing hydrophobically-modified iron oxide nanoparticles and amine-reactive Pluronic derivatives in an organic solvent, and subsequently emulsification in an aqueous chitosan solution by ultrasonication. The resultant shell cross-linked nanocapsules had a unique...

Iron oxide nanoparticles were synthesized and coated with silica by conventional coprecipitation method. Silica coated iron oxide nanoparticles were surface functionalized with chitosan. Silica coating and chitosan functionalization were confirmed by FTIR and TG-DTA analysis. XRD pattern revealed that the pure phase of Fe3O4 was retained even after coating. Particles of average size 12 nm were ...