carbon spheres were fabricated by hydrothermal method and their structural properties were investigated. carbon spheres with average sizes around of 230, 320 and 430 nm were synthesized in different concentration of glucose aqueous solution and different hydrothermal reaction time. the temperature of 180 °c by a hydrothermal reaction was fixed in all of glucose concentration and hydrothermal re...

Carbon Spheres were fabricated by hydrothermal method and their structural properties were investigated. Carbon Spheres with average sizes around of 230, 320 and 430 nm were synthesized in different concentration of glucose aqueous solution and different hydrothermal reaction time. The temperature of 180 °C by a hydrothermal reaction was fixed in all of glucose concentration and hydrothermal re...

In this study, carbon nano-micro spheres with tightly controllable size, regularand perfect shape, high yields and narrow size distribution were prepared simply fromglucose and DI water as precursors using a hydrothermal method. By setting the initialconcentration of glucose solution and changing the hydrothermal process time at aconstant temperature of 160 °C, carbon spheres with various sizes...

Mesoporous carbon spheres (MCS) have been fabricated from structured mesoporous silica sphere using chemical vapor deposition (CVD) with ethylene as a carbon feedstock. The mesoporous carbon spheres have a high specific surface area of 666.8 m2/g and good electrochemical properties. The mechanism of formation mesoporous carbon spheres (carbon spheres) is investigated. The important thing is a s...

Ostwald ripening is an evolutionary mechanism that results in micro-scale carbon spheres from nano-scale spheres. Vapor-phase carbon elements from small carbon nanoparticles are transported to the surface of submicron-scale carbon spheres, eventually leading to their evolution to micro-scale spheres via well-known growth mechanisms, including the layer-by-layer, island, and mixed growth modes. ...

In this study, carbon nano-micro spheres with tightly controllable size, regular and perfect shape, high yields and narrow size distribution were prepared simply from glucose and DI water as precursors using a hydrothermal method. By setting the initial concentration of glucose solution and changing the hydrothermal process time at a constant temperature of 160 °C, carbon spheres with various s...

Modified carbon spheres (CSPBs) were obtained by grafting poly(diallyl dimethyl ammonium chloride) (p-DMDAAC) on the surface of carbon spheres (CSs). It can be viewed as a kind of cation spherical polyelectrolyte brushes (CSPBs), which consist of carbon spheres as core and polyelectrolytes as shell. The method of synthesizing carbon spheres was hydrothermal reaction. Before the polyelectrolyte ...

Monodispersive carbon spheres with a high percentage of purity have been synthesized using a mixed-valent oxide-catalytic carbonization (MVOCC) process. In this paper, the chemical activities of the carbon spheres are examined by dispersing Pt, CdS and WO, nanoparticles, respectively, on the carbon surfaces from the microstructure information provided by transmission electron microscopy. The sp...

Colloidal carbon spheres were synthesized by the carbonization of squalane, a nonvolatile hydrocarbon solvent, in supercritical carbon dioxide. Precise pressure modulation of the fluid medium led to size controlled growth of carbon spheres ranging from 300 to 1500 nm in diameter. This unique synthetic approach of carbonizing a hydrocarbon suspension in supercritical fluid is found to suppress a...

N-doped carbon spheres with hierarchical micropore-nanosheet networks (HPSCSs) were facilely fabricated by a one-step carbonization and activation process of N containing polymer spheres by KOH. With the synergy effect of the multiple structures, HPSCSs exhibit a very high specific capacitance of 407.9 F g(-1) at 1 mV s(-1) (1.2 times higher than that of porous carbon spheres) and a robust cycl...