OBJECTIVE The main aim of this in vitro study was to evaluate the influence of Streptococcus mutans on the corrosion of titanium. METHODS S. mutans biofilms were formed on commercially pure titanium (CP-Ti) square samples (10mm×10mm×1mm) using a culture medium enriched with sucrose. Open circuit potential (OCP) and electrochemical impedance spectroscopy (EIS) measurements were used to evaluat...

OBJECTIVE This research was designed to investigate the effects of low pressure radio-frequency (RF) oxygen plasma treatment (OPT) on the surface of commercially pure titanium (CP-Ti) and Ti6Al4V. Surface topography, elemental composition, water contact angle, cell viability, and cell morphology were surveyed to evaluate the biocompatibility of titanium samples with different lengths of OP trea...

BACKGROUND Cobalt-chrome (CoCr) alloys have been used in dentistry in decades but very little is known about their behavior and biological impact as framework materials in implant dentistry. Furthermore, few studies have evaluated and compared the clinical and radiological results of abutment and abutment-free implant treatment concepts. AIMS To investigate in vitro CoCr and commercially pure...

OBJECTIVES Acid etching is a popular method to texture the surface of dental implants. During etching, the titanium oxide protective layer is dissolved and small native hydrogen ions diffuse into the unprotected implant surface. They enrich the implant surface with hydrogen and precipitate into titanium hydride (TiH). The aim of this study was to measure the concentration of TiH at the implant ...

PURPOSE The aim of the present study was to evaluate the biological response of alkali- and heat-treated titanium-8tantalum-3niobium surfaces by cell proliferation and alkaline phosphatase (ALP) activity analysis. METHODS Commercial pure titanium (group cp-Ti) and alkali- and heat-treated titanium-8tantalum-3niobium (group AHT) disks were prepared. The surface properties were evaluated using ...

Hafnium has been suggested as an interesting material for biomedical applications due to its good biocompatibility and osteogenesis. However, its behaviour under fretting corrosion conditions, found in applications such as dental and joint implants, has not been studied in depth. A three-electrode electrochemical cell integrated with a ball-on-flat reciprocating tribometer was used to investiga...

This study tested the following hypotheses: (1) acid-cleaned and passivated unalloyed titanium implants have higher surface energies (which are considered desirable for bone implants) than ethanol-cleaned titanium; (2) higher temperatures of heat treatment of unalloyed titanium result in higher surface energies; and (3) these changes can be related to changes in surface composition and roughnes...

The reaction of Cp*TiX3 [X ) Cl (1a), F (1b), Cp* ) η-C5Me5] with an excess of AlMe3 afforded the methylated products Cp*TiCl2Me (2a) and (Cp*TiF2Me)(AlMe2F) (2b), respectively, whereas under thermal conditions the reduced titanium species Cp*2Ti2(μ-Cl)6Al2Me4 (3) and Cp*2Ti2(μ-F)8Al4Me8 (4) were obtained in moderate yields. The reduction of Ti(IV) to Ti(III) is observed when Cp′2TiF2 (Cp′ ) η-...

The use of a single metal for all restorations would be necessary because it protects against metal corrosion caused by the contact of different metals. For this "one-metal rehabilitation" concept, non-alloyed commercially pure (CP) titanium should be used for all restorations. Titanium frameworks have been cast and used for the long term without catastrophic failure, whereas they have been fab...

Commercially pure titanium (cp-Ti) is widely used in the field of long-term clinical oral implantology owing to its ability to allow close bone-implant apposition. The optimization of its function based on artificial proteins has become a key issue in the development of improved cp-Ti implants. Here, we set out to identify peptide aptamers with preferential adsorption towards titanium-based imp...