Utilisation of fly ash and Ground Granulated Blast Slag as an alternative material in concrete reduces the use of OPC in concrete. Evolution of geopolymer concrete cured at ambient temperature broadens its suitability and applicability to concrete based structures. This paper presents the mix proportions and outcome of an experimental study on the density and compressive strength of geopolymer ...

Metakaolinite-based geopolymer has been synthesized at about 25 °C from metakaolin which has been calcined in different temperatures (600-900 °C) and different Na2O/SiO2 ratio activator (0.3-1.1). Compressive strength and microstructure of cement pastes after 7-28 days curing at ambient temperature were measured. Compressive strength tests on the samples showed that the sample made with calcine...

Geopolymer cement was evaluated as wellbore sealing material for carbon dioxide geosequestration application. Curing of cement system in saline water and strength testing in triaxial stress state condition under lateral confinement is relevant to primary cementing in CO2 geosequestration wellbore in saline aquifer. Geopolymer cement was cured in saline water (both at ambient conditions for 28 d...

OBJECTIVES Different light curing units are used for polymerization of composite resins. The aim of this study was to evaluate the degree of conversion (DC) and temperature rise in hybrid and low shrinkage composite resins cured by LED and Argon Laser curing lights. MATERIALS AND METHODS DC was measured using FTIR spectroscopy. For measuring temperature rise, composite resin samples were plac...

AIM The study compared pulp temperature rise during polymerization of resin-based composites (RBCs) using halogen and LED light-curing units (LCUs). METHODS AND MATERIALS A total of 32 teeth extracted from patients aged 11-18 years were used in the study. Thermocouples placed on the roof of the pulp chamber using a novel 'split-tooth' method. In Group 1 a halogen LCU with a light intensity of...

This paper aims to study the feasibility of highly conductive carbon fiber reinforced concrete (CFRC) as a self-heating material for ice formation prevention and curing in pavements. Tests were carried out in lab ambient conditions at different fixed voltages and then introduced in a freezer at -15 °C. The specimens inside the freezer were exposed to different fixed voltages when reaching +5 °C...

This paper presents a study on use of alkali activated bottom ash (BA) and ground granulated blast furnace slag (GGBS) blend in paver blocks. A preliminary effort on alkali-activated bottom ash, blast furnace slag based geopolymer (BA-GGBS-GP) mortar with river sand was carried out to identify the suitable mix for paver block. Several mixes were proposed based on the combination of BA-GGBS. The...

Bonding of polymer-based microfluidics to polymer substrates still poses a challenge for Lab-On-a-Chip applications. Especially, when sensing elements are incorporated, patterned deposition of adhesives with curing at ambient conditions is required. Here, we demonstrate a fabrication method for fully printed microfluidic systems with sensing elements using inkjet and stereolithographic 3D-print...

The introduction of affordable control networks for peanut dryers has made it possible to easily vary the curing temperature based on ambient air conditions. Previous research has used ambient temperature, relative humidity, and humidity ratio as possible control parameters. Peanuts from the same field were cured using four 0.11 m dryers to a moisture content of approximately 0.11 kg kg. Four d...