Purpose: Acrylic dentures frequently fracture during service due totheir poor strength characteristics. The aim of this study was to evaluate the effects of adding 5%, 10% and 15% aluminum oxide powder on the flexural strength, surface hardness of a conventional heat-polymerized acrylic resin. Materials and methods: One of the commonly used conventional heat cure denture base resin (DPI) and hi...

The reaction-bonded aluminum oxide (RBAO) process relies upon the oxidation of Al/Al2O3 powder compacts, and many of its associated advantages stem from the presence of the aluminum in the green powder. Higher aluminum contents in the starting powders allow for higher green strengths, densities, and lower overall shrinkage, all while producing a fine-grained, high-strength sintered material. Ho...

nano-sized γ-al2o3 was synthesized successfully by a simple method using al2(so4)3·18h2o as aluminium source and in the presence of polyethylene glycol (peg 2000). ftir spectroscopy, x-ray diffraction (xrd), scanning electron microscope (sem) and transmission electron microscope (tem) were used to characterize the structure and morphology of synthesized powder. the results showed that peg playe...

The introduction of air abrasion (sandblasting) technology to orthodontics may allow reaching optimum bond strength between the metal bracket and resin-modified glass ionomer cement. This study examined the effects of sandblasting metal bracket bases on the in vitro tensile bond strength of a resin-modified glass ionomer cement. Two-hundred foil-mesh based brackets were divided into ten groups ...

Nano-sized γ-Al2O3 was synthesized successfully by a simple method using Al2(SO4)3·18H2O as aluminium source and in the presence of polyethylene glycol (PEG 2000). FTIR spectroscopy, X-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscope (TEM) were used to characterize the structure and morphology of synthesized powder. The results showed that PEG playe...

The quality of the refractories applied on integrated gasification combined cycle should be a key factor that affects both the reliability and the economics of gasifier operation. To enhance the workability of chromia/alumina castables, three types of ultrafine alumina powder were added to improve the workability. Densification behavior of such castables in the presence of ultrafine alumina was...

Nano-sized γ-Al2O3 was synthesized successfully by a simple method using Al2(SO4)3·18H2O as aluminium source and in the presence of polyethylene glycol (PEG 2000). FTIR spectroscopy, X-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscope (TEM) were used to characterize the structure and morphology of synthesized powder. The results showed that PEG playe...

Alumina nanopowders produced by electrical explosion of wires were sintered using the spark plasma sintering technique. The results of XRD analysis show that the main phase in the compacted nanopowders is α-Al2O3. According to the SEM observations, the sintered alumina nanopowder consists of micron-sized faceted grains and nano-sized necked grains. The increase in sintering temperature resulted...

Polymer matrix composite materials that can emit radiation in the far-infrared region of the spectrum are receiving increasing attention due to their ability to significantly influence biological processes. This study reports on the far-infrared emissivity property of composite films based on far-infrared ceramic powder. X-ray fluorescence spectrometry, Fourier transform infrared spectroscopy, ...