Over the years, aluminum content in a vehicle part is increasing due to the needs to reduce weight as well as increase fuel efficiency. Most of the cast product in a vehicle part is mostly cast from A356 alloy. It is used because A356 alloy posses’excellent characteristics over other type of alloy such as cast ability, high weight-to-strength ratio, good corrosion resistance and good weld-abili...

The present study aims at developing A356/Al2O3(np) nano-composite with a novel and cost effective method for attaining homogeneous dispersion of Al2O3 nanoparticles in the Al matrix. In the current research, Al micro powders distributed on aluminum foil and then Al2O3 nanoparticles ultra-sounded in ethanol and sprayed on Al substrate. Subsequently, the sandwich foil was added to molten A356 du...

In recent years, improving the mechanical properties of metals has become the main challenge in the modern materials and metallurgical industry. An alloying process is usually used to achieve advanced performance of metals. This paper, however, describes an alternative approach. Modification with ceramic nanoparticles, gas-dynamic treatment (GDT) and a combined treatment were investigated on a ...

In this investigation ‚the fracture toughness of A356 containing15%SiC composite was studied. Al/SiC composites have been considered because of their mechanical and erosion properties .Low fracture toughness in Al/SiC as compared with Aluminium alloys is one of its disadvantage. In this study at first A356 alloy was melted in a smelting electrical furnace then poured into the mould. A356-15% Si...

During heat treatment, the work piece experiences a range of heating rates depending upon the sizes and types of furnace. When the Al-Si-Mg cast alloy is heated to the solutionizing temperature , recrystallization takes place during the ramp-up stage. The effect of heating rate on recrystallization in the A356 (Al-Si-Mg) alloy was studied using dilatometric and calorimetric methods. Recrystalli...

Al-Si-based casting alloys have a great potential in various industrial applications. Common strengthening strategies on these alloys are accompanied inevitably by sacrifice of ductility, known as strength-ductility trade-off dilemma. Here, we report a simple route by combining rapid solidification (RS) with a post-solidification heat treatment (PHT), i.e. a RS + PHT route, to break through thi...

The objective of the present work is to study the casting characteristics of various A1-Li alloys, which include fluidity and strengths of the alloys and their interaction with cast molds. Materials investigated are Al-Li-Mg and Al-Li-Cu-Mg alloys with Li content of 2.5 wt%. The results show that sand molds with resin binders are good for A1-Li casting. Ceramic coatings can further reduce the m...

The influences of age hardening and HIP (Hot Isostatic Pressing) on the mechanical properties of A356 (Al 7Si 0.6 Mg) casting alloys were studied. Cast bars were homogenized, heated and maintained at a temperature of 540°C for a duration of 2 hours, followed by rapid cooling in a polymeric solution. The castings were age hardened at 180°C for a duration of 4 hours before being subjected to HIP ...