In this research, the fabrication of MCM-41 mesoporous material nanofibers by an electrospinning technique was performed. The MCM-41 nanofibers (MCM-41 NFs) as a novel host on the incorporation of silver has been studied in [Ag(NH3)2]NO3 precursor solution through the heat-treatment process. The formation of silve...

Copper particles were incorporated into nanofibers during the electrospinning of poly-D,L-lactide (PDLLA) and poly(ethylene oxide) (PEO). The ability of the nanofibers to prevent Pseudomonas aeruginosa PA01 and Staphylococcus aureus (strain Xen 30) to form biofilms was tested. Nanofibers containing copper particles (Cu-F) were thinner (326 ± 149 nm in diameter), compared to nanofibers without c...

electrospinning was applied to nitrocellulose (nc) solutions  in dmf, dmso  and  ethyl  methyl  keton  to  obtain  nc  nanofibers. electrospraying  process  was  observed  when  dmf  was  used  as solvent.  in  comparison  to nc/dmf, nc/dmso  solution  resulted  in the  formation  of  a  coating  film  as  indicate  by  sem.  two  different electrospun  nanofibers,  smooth  nanofibers  with  90...

objective(s): to improve water stability of electrospun chitosan/ polyethylene oxide (peo) nanofibers, genipin, a biocompatible and nontoxic agent, was used to crosslink chitosan based nanofibers.  materials and methods: different amounts of genipin were added to the chitosan/peo solutions, chitosan/peo weight ratio 90/10 in 80 % acetic acid, and the solutions were then electrospun to form nano...

25 Electrospinning of polymer solutions or melts driven by a high26 voltage electric charge is a highly versatile technique that can be used 27 to generate continuous 1D polymeric fibers with diameters rang28 ing from several micrometers to tens of nanometers. Electrospun 29 nanofibrous materials possess a variety of interesting characteristics 30 such as small dimension, large specific surface...

The goal of this research was to investigate the potential of newly synthesized gold complex trichloro(2,4,6-trimethylpyridine)Au(III) as an anticancer agent. The gold(III) complex was synthesized and grafted on nanoporous silica, MCM-41, to produce AuCl(3)@PF-MCM- 41 (AuCl(3) grafted on pyridine-functionalized MCM-41). The toxicity of trichloro(2,4,6- trimethylpyridine)Au(III) and AuCl(3)@PF-M...

Surface modified electrospun polyester (PET) nanofibers with cyclodextrin polymer (CDP) were produced (PET/CDP). CDP formation onto electrospun PET nanofibers was achieved by polymerization between citric acid (CTR, crosslinking agent) and cyclodextrin (CD). Three different types of native CD (α-CD, β-CD and γ-CD) were used to form CDP. Water-insoluble crosslinked CDP coating was permanently ad...

Superfine Particles (SP) of soluble eggshell membrane and medical grade polyurethane (MPU) blend nanofibers were prepared by electrospinning different blend ratios of SP/MPU suspensions for regeneration of the natural fiber-like structure of the eggshell membrane. The addition of SP had no obvious effect on the electrospinning process of MPU nanofibers, and the SP were randomly dispersed in the...

The electrospinning technique is a versatile method for the production of fibrous scaffolds able to resemble the morphology of the native extra cellular matrix. In the present paper, electrospinning is used to fabricate novel SiO2 particles (type MCM-41) containing poly(epsilon-caprolactone) (PCL) fibers. The main aims of the present work are both the optimization of the particle synthesis and ...

Titanium dioxide-polyaniline/polyamide 6 (TiO(2)-PANI/PA6) composite nanofibers were prepared by in situ polymerization of aniline in the presence of PA6 nanofibers and a sputtering-deposition process with a high purity titanium sputtering target. TiO(2)-PANI/PA6 composite nanofibers and PANI/PA6 composite nanofibers were fabricated for ammonia gas sensing. The ammonia sensing behaviors of the ...