In this paper, the corrosion residual strength of the AZ91D magnesium alloy in the presence of sulfate-reducing bacteria is studied. In the experiments, the chemical composition of corrosion film was analyzed by a scanning electron microscope with energy dispersive X-ray spectroscopy. In addition, a series of instruments, such as scanning electronic microscope, pH-meter and an AG-10TA materials...

* Corresponding author. Tel: 34 1 3944348; Fax: 34 1 3944357 E-mail: [email protected] ABSTRACT X-ray photoelectron spectroscopy (XPS) was used in order to investigate the correlation between the surface chemistry and the atmospheric corrosion of AZ31, AZ80 and AZ91D magnesium alloys exposed to 98% relative humidity at 50oC. Commercially pure magnesium, used as the reference material, reveale...

The present work uses X-ray photoelectron spectroscopy (XPS) analysis to compare the chemical composition of native oxide films formed spontaneously on commercial pure magnesium and AZ31, AZ80 and AZ91D magnesium alloys. The study considers both the outer surface and inner regions of the films with the assistance of argon ion bombardment. Possible relationships are established between the alloy...

The protective performance of zeolite coating on AZ91D magnesium alloy was evaluated using potentiodynamic polarisation and electrochemical impedance spectroscopy (EIS) in 0.1 M sodium chloride solution (NaCl). Electrical equivalent circuit (EEC) was developed based upon hypothetical corrosion mechanisms and simulated to correspond to the experimental data. The morphology and the chemical natur...

Tensile specimens of nonflammable AZ91D Mg alloy were fabricated in this study via cold chamber die-casting process. Dimensions of tensile specimens were 25mm in length, 4mm in width, and 0.8 or 3.0mm in thickness. Microstructure observation was conducted before and after tensile tests at room temperature. In the die casting process, various injection distances from 150 to 260mm were employed t...

A method is presented to use a dimensionless form of the well-known Niyama criterion to directly predict the amount of shrinkage porosity that forms during solidification of metal alloy castings. The main advancement offered by this method is that it avoids the need to know the threshold Niyama value below which shrinkage porosity forms; such threshold values are generally unknown and alloy dep...

Blown-powder laser surface alloying was performed on the magnesium alloy AZ91D with Al-Si alloy powder to improve corrosion resistance. Characterization by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and x-ray diffraction (XRD) analysis revealed that intermetallic compounds (IMCs) of Mg2Si, Al12Mg17 and Al3Mg2 were formed in the matrix of α-Mg and Al solid solutions...

Phase equilibria of AZ91D Mg alloys for nonflammable use, containing Ca and Y, were carried out by using FactSage® and FTLite database, which revealed that solid solution treatment could be performed at temperatures from 400 to 450C. Solid solution treatment of AZ91D Mg alloy without Ca and Y was successfully conducted at 420C and supersaturated microstructure with all beta phase resolved into ...

Abstract Magnesium alloy has excellent physical and mechanical properties is expected to become a new generation of medical degradable materials. In this paper, the blood compatibility analysis Graphene Oxide(GO) / Hydroxyapatite(HA)-AZ91D was carried out improve magnesium AZ91D used as control group GO/HA-AZ91D experimental group. The two samples were studied in vitro by hemolysis rate test, c...

Magnesium alloys have considerably lower density than the aluminum alloy matrices that are typically used in syntactic foams, allowing for greater specific energy absorption. Despite the potential advantages, few studies have reported the properties of magnesium alloy matrix syntactic foams. In this work, Al₂O₃ hollow particles of three different size ranges, 0.106-0.212 mm, 0.212-0.425 mm, and...