The aim of this work is to determine the fatigue life of 316L stainless steel. The mechanisms of fatigue of 316L stainless steels were investigated and discussed. The fatigue tests were carried out at constant-amplitude cyclic loading with load ratio R=0.1. Scanning Electron Microscope (SEM) is then used to examine the fracture surface. The results show that the fatigue limit of 316L stainless ...

Stainless steels have good corrosion resistance in many environments but welding or aging can decrease their resistance. This work focused on the effect of aging time and ultrasonic nano-crystal surface modification on the passivation behavior of 316L stainless steel. In the case of slightly sensitized 316L stainless steel, increasing the aging time drastically decreased the pitting potential, ...

An attempt made to optimize the operating parameters involved in an autogenous pulsed Nd: YAG laser welding process of similar and dissimilar combinations of butt joint of 2 mm thick 316 L stainless steel and mild steel. Influence of prominent laser welding parameters such as average peak power, defocus position, spot position, and shielding gas were investigated for welded joints considered. T...

INTRODUCTION Intravascular coronary stenting has been used in the treatment of coronary artery disease (CAD), with a major limitation of in-stent restenosis (ISR). The 316 stainless steel has been widely used for coronary stents. In this study, we developed a novel coating method to reduce ISR by simultaneously coating vascular endothelial growth factor (VEGF) and anti-CD34 antibody on 316L sta...

To evaluate the clinical potential of high nitrogen nickel-free austenitic stainless steel (HNNF SS), we have compared the cellular and molecular responses of human umbilical artery smooth muscle cells (HUASMCs) to HNNF SS and 316L SS (nickel-containing austenitic 316L stainless steel). CCK-8 analysis and flow cytometric analysis were used to assess the cellular responses (proliferation, apopto...

The polarisation characteristics of the electropolishing process in a magnetic field (MEP – magnetoelectropolishing), in comparison with those obtained under standard/conventional process (EP) conditions, have been obtained. The occurrence of an EP plateau has been observed in view of the optimization of MEP process. Up-to-date stainless steel surface studies always indicated some amount of fre...

Orthodontic stainless-steel appliances are considered to be corrosion resistant, but localized corrosion can occur in the oral cavity. This study was undertaken to evaluate the properties of super stainless steels in orthodontic applications. Accordingly, the metallurgical properties, mechanical properties, corrosion resistance, amount of the released nickel, cytotoxicity, and characteristics o...

Initiation of corrosion on reinforcing bars occurs when a critical chloride concentration is achieved. A universal value for the chloride concentration that causes depassivation has not been agreed upon for carbon steels due to a variety of experimental factors. The chloride threshold depends on the rebar material, rebar surface condition, testing environment, method of detection, definition of...

The effect of several Almen intensities of shot peening on the corrosion behavior, surface roughness, micro hardness profiles, and residual stresses of stainless steel AISI 316 L were investigated. Hydroxyapatite coating (HA) were applied to shot peened materials to improve their corrosion resistance. The corrosion behaviour were studied using potentiodynamic polarization. The electrochemical t...

This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC) in a nitrite-containing chloride solution. Slow strain rate testing (SSRT) in 30 wt. % MgCl₂ solution established SCC susceptibility, as evidenced by post-SSRT fractography. Addition of nitrite to the chloride solution, which is reported to have inhibitive influence on corrosion of stainless ste...