FePt single-layer and FePt–Fe multilayer thin films are prepared by magnetron sputtering. By varying the Pt content, FePt, Fe3Pt, or a mixture of FePt and Fe3Pt can be obtained in Fe–Pt single layers. In annealed FePt–Fe multilayers, the coercivities decrease with the introduction of Fe layers compared to FePt single layers, while the magnetization increases. The single-phase behavior of the hy...

In this work Ag underlayers, with a slightly larger unit cell than FePt, were found not only to induce epitaxial growth of the FePt films but also to reduce the FePt ordering temperature. Without using the Ag underlayer, the FePt film deposited onto the Si substrate was fcc disordered. By the use of the Ag underlayer, it was observed that the FePt unit cells were expanded in the film plane. Thi...

FePt and FePt/Cr films were epitaxially grown on MgO (2 0 0) substrates at 350 1C by DC magnetron sputtering. The structural properties and epitaxial relationship are investigated by high-resolution X-ray diffraction (XRD). The XRD spectra revealed that both FePt and FePt/Cr films had a (0 0 1) preferred orientation. However, FePt films with Cr underlayers had a larger a and a smaller c than th...

FePt/iron oxide core/shell nanoparticles are synthesized by a two step polyol process with 1,2hexadecanediol as the reducing reagent. Monodispersed 2.6-nm FePt nanoparticles are first obtained by reduction of iron(III) acetylacetonate and platinum(II) acetylacetonate. These preformed FePt nanoparticles are then used as seeds and an iron oxide shell is formed in the second synthesis step. The ro...

Nano-sized FePt capsules with two types of ultrathin shell were fabricated using a template method for use in a nano-scale drug delivery system. One capsule was composed of an inorganic-organic hybrid shell of a water-soluble polymer and FePt nanoparticles, and the other capsule was composed of a network of fused FePt nanoparticles. We demonstrated that FePt nanoparticles selectively accumulate...

In this work, Ag underlayers, which have a slightly larger lattice parameter than FePt, were found not only to induce epitaxial growth of the FePt films but also to reduce the temperature at which the atomic ordering occurred. Without using the Ag underlayer, the FePt film deposited onto the hydrofluoric acid etched-Si substrate was FCC disordered. When Ag underlayers were used the FePt unit ce...

The effects of Ru and Ag cap layers on the microstructure and magnetic properties of the FePt ultrathin films have been investigated. The results indicate that i) The Ag cap layer segregates from the FePt/Ag bilayer, lowers the FePt ordering temperature, promotes the FePt thin films to form island structure, and enhances the coercivity; ii) The Ru cap layer increases the FePt ordering temperatu...

Nanomaterials have an advantage in "personalized" therapy, which is the ultimate goal of tumor treatment. In order to investigate the potential ability of FePt nanoparticles (NPs) in the diagnosis and chemoradiotherapy treatment of malignant tumors, superparamagnetic, monodispersed FePt (~3 nm) alloy NPs were synthesized, using cysteamine as a capping agent. The NPs were characterized by means ...