The photocatalytic decomposition of 2-, 3and 4-chlorobenzoic acids (2CB, 3CB and 4CB, respectively) with TiO2 loaded on HZSM-11 zeolite was investigated. The optimum decomposition rate of 2CB was obtained with TiO2/HZSM-11(30%) (TiO2 30 wt.%) catalyst at a concentration of 1 mg mL. 2CB and 3CB decompose at similar rates, but 4CB remains adsorbed on TiO2/HZSM-11(30%) without further degradation....

Dehydroaromatization of methane (DHAM) under non oxidative condition was studied over tungsten loaded HZSM-5 catalysts to produce aromatic hydrocarbons. The catalysts were prepared by impregnation method using different conditions: in neutral and acidified solution. The activity of W/HZSM-5 prepared by neutral solution and W-H2SO4/HZSM-5 prepared in acidified condition were compared. The result...

Nanocrystal HZSM-5 zeolite aggregates with different SiO2/Al2O3 molar ratios were prepared under low temperature and were used to catalyze the conversion of methanol to propylene and butene. The coke location, coke content, and coke species deposited on HZSM-5 aggregates were investigated. The near-graphite carbon on the external surface of HZSM-5 zeolite (SiO2/Al2O3 molar ratio = 400) was dist...

A compound catalyst (RA) consisted of Ni, ZnO and HZSM-5 with functions of reactive adsorption desulfurization (RADS) and olefin aromatization for fluid catalytic cracking (FCC) gasoline upgrading was prepared. X-ray powder diffraction (XRD), temperature-programmed reduction and low-temperature N2 adsorption were used to characterize the properties of the catalysts. Performance evaluation by FC...

Catalytic cracking of butene to propylene was carried out in a continuous-flow fixed-bed reactor over HZSM-5 catalysts modified by nickel and phosphorus. The structure and acidity of catalysts were measured by N2 adsorption, NH3-TPD and XPS. The results revealed that surface area and strong acid sites both decreased with increasing phosphorus loadings. The increment of phosphorus loadings reduc...

Ex situ catalytic pyrolysis of Citrus unshiu (C. unshiu) peel was performed using a tandem μ-reactor-GC/MS consisting of two sequential furnaces. The pyrolyzates of C. unshiu peel, composed mainly of alcohols, ketones and furans produced in the 1st furnace of the reactor, were upgraded to aromatics by the use of catalysts in the 2nd furnace. Compared to wood powder, C. unshiu peel produced larg...

The effects of process variables (temperature, space velocity, water addition and Si/Al ratio) on the conversion of acetone to aromatic chemicals have been investigated. The reaction is carried out by fixed bed reactor at an atmospheric pressure to examine the activity and selectivity of HZSM-5. The results show that HZSM-5 exhibited a high active and a shape-selective catalyst for the formatio...

Hydrothermally synthesized high silica borosilicates with the MFI structure was subjected to several characterization techniques. The effect of boron on the structure and acidity of HZSM-5 catalyst were studied by XRD, SEM, N2 adsorption, solid state NMR, NH3-TPD. It was confirmed that boron had entered the framework in the boron samples. The results also revealed that strong acidity was weaken...