Corrosion inhibitory impacts of turmeric with concentrations of 200-800 ppm on the electrochemical behavior of mild steel were studied in the medium of NaCl 3.5% using several techniques such as electrochemical impedance spectroscopy (EIS) and polarization. Scanning electron microscopy (SEM) was used for analyzing the surface of mild steel after 24 hours of immersion in the electrolyte solution...

In the present study NiCrAlY bond coating layer was produced by electroplating against common atmospheric plasma spraying (APS). Both types of the bond coats were applied on IN738LC base metal then, the YSZ (ZrO2-8% Y2O3) thermal barrier top layer was coated by atmospheric plasma spray technique. Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come ...

The roles of the alloying elements Mo, Cr, and W in resisting crevice corrosion of UNS N06022, UNS N06625, and UNS N10362 have been studied under galvanostatic conditions in 5 mol/L NaCl at 150°C. Corrosion damage patterns were investigated using surface analytical techniques such as scanning electron microscopy and optical imaging, and the corrosion products characterized by energy dispersive ...

A new experimental method was applied in in situ corrosion monitoring of mild steel Q235 under alternate wet-dry conditions. The thickness of the electrolyte film during the wet cycle was monitored by a high-precision balance with a sensibility of 0.1 mg. At the same time, an electrochemical impedance technique was employed to study the effect of film thickness on corrosion rates. Experimental ...

Pre-plated leadframes packages with a new noble metal finish type were exposed to various electrochemical migration tests, and mixed flowing gas environments to assess the quality and reliability due to these environmental conditions. Packages were tested as discrete parts and also as parts mounted onto printed circuit boards to assess the effect of reflow soldering. Selected packages with SnPb...

Tapping mode atomic force microscopy (TM-AFM) was used for the investigation of the early stages of atmospheric corrosion of pure copper and pure iron. The information obtained by this method is the change of the topography of the sample surfaces with emphasis on the shape and lateral distribution of the corrosion products grown within the first 1300 min of weathering. Investigations were carri...

EXAFS measurements in the corrosion deposits were performed on Bell Labs-UIUC beamline X16C at the NSLS at Brookhaven National Laboratory in grazing incidence fluorescence mode at room temperature. EXAFS in the reference Cu and Pb metal foils, malachite, cerussite and hydrocerussite were measured in transmission. Sagittally focused second crystal in the double crystal Si (111) monochromator all...