The purpose of this study is to evaluate the fitting accuracy and fracture resistance of crowns using a hybrid zirconia frame made of both porous and dense zirconia. Commercial semi-sintered zirconia, sintered dense zirconia and sintered hybrid zirconia were used. Sintered zirconia was milled using the CAD/CAM system, and semi-sintered zirconia was milled and sintered to fabricate molar crown f...

This study evaluated the effect of a) pontic materials and b) occlusal morphologies on the fracture resistance of fi ber-reinforced composite (FRC) inlay-retained fixed dental prostheses (FDP). Inlay-retained FRC FPDs (N=45, n=9) were constructed using a) resin composite (deep anatomy), b) natural tooth, c) acrylic denture tooth, d) porcelain denture tooth and e) resin composite (shallow anatom...

During the past decade, zirconia-based ceramics have been successfully introduced into the clinic to fabricate fixed dental prostheses (FDPs), along with a dental computer-aided/computer-aided manufacturing (CAD/CAM) system. In this article (1) development of dental ceramics, (2) the current status of dental CAD/CAM systems, (3) CAD/CAM and zirconia restoration, (4) bond between zirconia and ve...

PURPOSE The aim of this in vivo study was to evaluate the clinical performance of porcelain veneers after 5 and 10 years of clinical service. MATERIALS AND METHODS A single operator placed porcelain laminates on 87 maxillary anterior teeth in 25 patients. All restorations were recalled at 5 years and 93% of the restorations at 10 years. Clinical performance was assessed in terms of esthetics,...

also often required even in the posterior region. However, all-ceramic crowns pose some problems, including weak mechanieal properties and occurrence of cracks or pores in the erown that could ultimately lead to fracture oi' the restorationii'. Thus far, all-ceramic crowns have been fabricated by firing porcelain manuaNy onto a refractory die, or by casting or heat-pressing the cerarnics. Howev...

STATEMENT OF PROBLEM Zirconia-based restorations have the common technical complication of delamination, or porcelain chipping, from the zirconia core. Thus the shear bond strength between the zirconia core and the veneering porcelain requires investigation in order to facilitate the material's clinical use. PURPOSE The purpose of this study was to evaluate the bonding strength of the porcela...

The authors’ intention was to present ceramic restoration repair as a reliable, low-cost and low-risk procedure, by demonstrating 3 cases in the aesthetic zone. Intraoral ceramic repair was chosen for the small porcelain fracture of the maxillary left central incisor and for the large porcelain surface detachment of the maxillary left lateral incisor, since patients did not want to replace the ...

In all-ceramic restorations, crack formation and propagation phenomena are of major concern, since they may result in intra-oral fracture. The objective of this study was calculation of damage in porcelain MOD inlays by utilization of a finite-element (FE) implementation of the distributed crack theory. "Damage" is defined as the parameter that describes the local decrease of stiffness caused b...