BACKGROUND The aim of the study was to evaluate, in vitro, the surface roughness of two composite resins submitted to simulated toothbrushing with three different dentifrices. MATERIALS AND METHODS Totally, 36 samples of Z350XT and 36 samples of Empress Direct were built and randomly divided into three groups (n = 12) according to the dentifrice used (Oral-B Pro-Health Whitening [OBW], Colgat...

Background and aims. Polymerization efficacy affects the properties and performance of composite resin restorations.The purpose of this study was to evaluate the effectiveness of polymerization of two micro-hybrid, two nano-hybrid and one nano-filled ormocer-based composite resins, cured by two different light-curing systems, using Fourier transformation infrared (FT-IR) spectroscopy and Vicker...

This study observed alteration in the radiopacity and microhardness of expired resin-based materials compared to non-expired materials and the operating characteristics of the X-ray source used. Five 2 mm-thick cured specimens were prepared for each material: composite resins (P60®, Z100®), and a compomer (Dyract AP®). Radiopacity of the specimens was evaluated comparing the density of the resi...

This study investigated weight changes of seven different light-cured composite restorative materials, one polyacid glass ionomer compomer, and one light-cured glass-ionomer cement following short-term and long-term storage in water. Two packable composites, three universal (hybrid) composites, one microglass composite, one polyacid glass ionomer resin composite (compomer), one microhybrid low-...

The aim of this study was to analyze the diametral tensile strengths of three resin-modified restorative glass ionomer cements--Vitremer, Fuji II LC and Photac Fil and one compomer--Dyract. They were tested at 1 hour, 1 day and 1 week. Kratos testing machine was used to load the specimens at a cross-head speed of 0.5 mm/min. The data were analyzed by two-way ANOVA and Tukey's test that showed s...

OBJECTIVE To compare wear performance and resistance to crack propagation (K1C) of commercial restorative materials and their flowable variations. A potential correlation between three-body wear and fracture toughness, modulus of elasticity, fracture work, Vickers hardness, and filler content was investigated. METHOD AND MATERIALS Seven restoratives (five composites, one ormocer, and one comp...

AIM Despite the improvements to compomer materials, the bond strength of these materials remains inferior to "composite/resin bonding" systems and limits their clinical use. The purpose of this study was to evaluate the effect of acidic conditioning with phosphoric acid and Prompt L-Pop (PLP) on the shear bond strength of two compomers Dyract AP (DAP) and Composan Glass (CG) to dentin. METHOD...

current study is aimed to compare fluride release in conventional glass ionomer, light-cured glass ionomer and compomers. standard samples from the aforementioned materials were prepared and measured by selective fluride ion electrode in intervals of 24hours, 1,2,3 and 4 weeks in neutral ph of 7 and acidic ph of 4.5. the obtained data represented that fluride ion release decreased in time but t...

The mechanical properties of the light-cured composite resins are related to the material composition, but also vary according to the light-source characteristics used for polymerization. In this study we followed the compressive strength variation for a light-cured composite resin according to the time of exposure to the curing light. With that end in view,18 test pieces were made from a light...