The corrosion behavior of three sorts of refractories based on alumina-graphite were studied by immersion tests. The melts included smelting reduction molten slag and corresponding carbon saturated molten iron. The influence of test temperature, FeO content in slag and specimen rotative velocity on the corrosion rate of refractories was examined. By means of SEM and EDS, the microstructure chan...

diamond like carbon (dlc) film was grown by hot filament chemical vapor deposition (hfcvd)technique. in the present work, we investigated the quality of the dlc films groew on the substratesthat were coated with various metal nanocatalysts (au and ni). a combination of ch4/ar/h2 rendersthe growth of carbon nanostructures technique (diamond like carbon). the utilized samples werecharacterized by...

OBJECTIVES Five commercial dental silanes were evaluated in vitro as adhesion promoters bonding a luting cement to silica-coated titanium surfaces. METHODS Titanium slides (n=20) were cleaned with alumina sand and then silica-coated with a special sand consisting of alumina particles coated with silica. The bonding of a resin composite cement (3M ESPE, Seefeld, Germany) to silica-coated and s...

nanostructured alumina thin films were coated on stainless steel by sol-gel dip coating method. in order to prevent crack formation, al2o3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. effects of calcination temperature and withdrawal speed on structural properties were analyzed using xrd and sem. topography and thickness of coatings were analyzed by ...

background: titanium (ti) implants are commonly coated with hydroxyapatite (ha). however, ha has some disadvantages such as brittleness, low tensile strength and fracture toughness. it is desirable to combine the excellent mechanical properties of zro2 and the chemical inertness of al2o3 with respect to the purpose of this project which was coating ti implants with ha-zro2-al2o3 to modify the s...

in this work, a simple and effective way to modify the support surface is developed and a nanostructure ceramic support to facilitate deposition of a defect-free overlying micro and meso (nano) porous membrane is obtained. to achieve high performance nanocomposite membranes, average pore size of outer surface of support was reduced by dip-coating in submicron and nano α-alumina slurries. in thi...

In the present study, the effect of alumina on the pore structure and hydrothermal stability of nanostructured silica was investigated. SiO2 and SiO2-15wt%Al2O3 membranes were prepared by dip coating on mesoporous γ-Al2O3 coated macroporous α-alumina support. The particle sizes of sol were increased by adding of alumina to silica...

A well-designed type of ultrathin carbon shell coating a silver core was prepared for the first time through an alternate adsorption and carbonization method. The obtained ultrathin carbon shell shows prominent advantages, including sufficient uniformity, better chemical stability than silica or alumina, biocompatibility, being free of pin-holes and low cost.