The solid state reactions and structural evolution in nanocrystalline FePt powders during mechanical ball milling at 77 K and subsequent annealing have been investigated. Above 310 °C the formation of L10 FePt is observed. As the milling time increases, the enthalpy evolved during the transformations is reduced, whereas the corresponding activation energy increases. For accelerating the orderin...

Magnetic nanoparticles and thin films exhibiting a large magnetic anisotropy energy density (MAE) have attracted enormous attention over the last years due to their potential use in magnetic data storage or sensing applications. FePt alloy nanoparticles and films have a huge MAE in the chemically ordered L10 phase. This ordered phase is typically obtained by annealing the as-prepared chemically...

In situ ordering of FePt thin films by sputtering onto Ag/Si and Ag/Mn3Si/Ag/Si templates has been demonstrated. Due to the evolution from island-like to a continuous film structure as a function of Ag thickness, the ordering and orientation of the FePt films both change with Ag thickness. A continuous (002) Ag film results in a greater L10 phase formation with -axis oriented both perpendicular...

Chemical reduction of ferric acetylacetonate (Fe(acac)3) and platinum acetylacetonate (Pt(acac)2) using polyol as a reducing agent as well as an effective surfactant, has successfully yielded monodisperse FePt nanoparticles with a size of approximately 2 nm. When annealed samples were compared to FePt nanoparticles synthesized using oleic acid and oleylamine as the surfactants under identical c...

Texture formation in FePt thin films via thermal stress management" (2005).

Hard-magnetic nanomaterials like nanoparticles of FePt are of great interest because of their promising potential for data storage applications. The magnetic properties of FePt structures strongly differ whether the crystal phases are face centered cubic (fcc) or face centered tetragonal (fct). We evaluated aberration corrected HRTEM, electron diffraction and aberration corrected HAADF-STEM as ...

Ion implantation is a promising technique for fabricating high density bit patterned media (BPM) as it may eliminate the requirement of disk planarization. However, there has not been any notable study on the impact of implantation on BPM fabrication of FePt, particularly at nano-scale, where the lateral straggle of implanted ions may become comparable to the feature size. In this work, implant...

We demonstrate a novel high-performance DNA hybridization biosensor with a carbon nanotubes (CNTs)-based nanocomposite membrane as the enhanced sensing platform. The platform was constructed by homogenously distributing ordered FePt nanoparticles (NPs) onto the CNTs matrix. The surface structure and electrochemical performance of the FePt/CNTs nanocomposite membrane were systematically investig...

The electrocatalytic oxidation of formic acid at a gold electrode functionalized with FePt nanoparticles was studied by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) in a mixed solution of 0.1 M HCOOH and 0.1 M HClO4. The FePt bimetallic nanoparticles, with a mean diameter of 3 nm, were prepared by a chemical reduction method. The Au/FePt nanostructured electrode was ...

High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction pressure and temperature. Density of the bulk samples up to 95% theoretical value has been obtained while the nanostructured morphology is retained. It is also observed that a hig...