background: the clinical success of sandwich technique depends on the strength of resin-modified glass ionomer cement (rmgic) bonding to both dentin and resin composite. therefore, the shear bond strength (sbs) of resin composite bonded to rmgic utilizing different resin adhesives versus a gic-based adhesive was compared. materials and methods: in this in vitro study, 84 holes (5×2 mm) were pre...

PURPOSE This study aimed to investigate whether dentin surface preparation with diamond rotary instruments of different grit sizes affects the shear bond strength of resin-bonded restorations. MATERIALS AND METHODS The buccal enamel of 60 maxillary central incisors was removed with a low speed diamond saw and wet ground with silicon carbide papers. The polished surfaces of the teeth were prep...

The flexural strength and flexural modulus of an experimental metal-resin composite, which used Ag-In alloy particle as the filler, were evaluated. The effect of acid treatment and heat treatment on the Ag-In alloy particle was investigated. The flexural strength of the experimental metal-resin composites ranged from 65.5 MPa to 91.0 MPa. The flexural strength of the metal-resin composite incre...

statement of problem: fracture strength of a denture base resin is of great concern, and many approaches have been used to strengthen acrylic resin dentures. purpose: the aim of this study was to measure the transverse strength of a heat polymerized acrylic resin, after reinforcement with metal wire and two types of glass fibers. materials and methods: forty rectangular specimens (65.0×10.0×3.3...

Abstract This article proposes the preparation and microwave thermal cured (MTC) epoxy-modified phenolic fibers for first time. Epoxy-modified thermoplastic resin was prepared in acidic condition using phenol, formaldehyde, epichlorohydrin as reactants, then underwent additive reaction with formaldehyde to obtain thermosetting resin, which converted into nascent through wet spinning. Finally, w...

This in vitro study evaluated the effect of tooth age on the tensile bond strength of Prime & Bond NT adhesive system to dentin. Human third molars from the five age groups were analyzed: A- 17 to 20yrs, B- 21 to 30yrs, C- 31 to 40yrs, D- 41 to 50yrs and E- 51 to 63yrs. The occlusal enamel was removed using a diamond saw under water cooling and the dentin surface was wet-ground with 600-grit Si...

introduction: the aim of this in vitro study was to evaluate the effect of mta-based sealer (mta fillapex), eugenol-based sealer (dorifill) and an epoxy resin sealer (ah plus) on the bond strength of fiber posts cemented with a self-etch adhesive. materials and methods: the root canals of 72 maxillary incisors were prepared using the step-back technique after removing/cutting off the crowns. th...

bioactive glass air abrasion is a conservative technique to remove initial decalcified tissue and caries. this study examined the shear bond strength of composite resin to sound and decalcified enamel air-abraded by bioactive glass (bag) or alumina using etch-and-rinse and self-etch adhesives.forty-eight permanent molars were root-amputated and sectioned mesiodistally. the obtained 96 specimens...

PURPOSE The purpose of this study was to evaluate and compare the flexural strength and microhardness of provisional restorative materials fabricated utilizing rapid prototyping (RP), Computer Assisted Designing and Computer Assisted Milling (CAD-CAM) and conventional method. MATERIALS AND METHODS Twenty specimens of dimensions 25 mm × 2 mm × 2 mm (ADA-ANSI specification #27) were fabricated ...

This study aimed to evaluate the tensile and transverse bond strength of chairside reline resins (Tokuyama Rebase II, Mild Rebaron LC) to a thermoplastic acrylic resin (Acrytone) used for non metal clasp denture. The results were compared with those of a conventional heat polymerized acrylic resin (Paladent 20) and a thermoplastic polyamide resin (Biotone). The failure sites were examined by sc...