ID No : 43 ABSTRACT Concrete tends to crack due to its relatively low tensile strength which jeopardizes the good condition of steel reinforcement bars. Concrete cracks start at micro level and facilitate ingression of corrosive substances such as SO4 , Cl, O2. Corrosion of the rebar may result in failure of the structure. Self-healing concrete can provide crack repair immediately after crack i...

Computational models based on the finite element method and linear or nonlinear fracture mechanics are herein proposed to study the mechanical response of functionally designed cellular components. It is demonstrated that, via a suitable tailoring of the properties of interfaces present in the mesoand micro-structures, the tensile strength can be substantially increased as compared to that of a...

An elastic-plastic analysis is performed for two problems relevant to fracture mechanics: a semi­ infinite body with an edge crack in a far out-of-plane shearing field and an infinite plate under plane stress conditions containing a finite line crack in a remote tensile field. Amplitudes of the dominant singularity in the plastic region at the crack tip, the plastic stress and strain intensity ...

This study focuses on the effect of the amount of silica fume addition and volume fraction of steel fiber on the engineering properties of cementitious materials. Test variables include dosage of silica fume (5% and 10%), water/cement ratio (0.35 and 0.55) and steel fiber dosage (0.5%, 1.0% and 2.0%). The experimental results included: compressive strength, direct tensile strength, splitting te...

An integrated manufacturing process simulation framework has been developed to predict the trimmed edge tensile stretchability of AA6111-T4 sheets by incorporating the burr geometry, damage, and plastic strain from trimming simulations into subsequent tensile stretchability simulations. The influence of the trimming die clearances on the predicted tensile stretching ductility (stretchability) i...

AN EXACT asymptotic analysis is presented of the stress and deformation fields near the tip of a quasistatically advancing plane strain tensile crack in an elastic-ideally plastic solid. In contrast to previous approximate analyses, no assumptions which reduce the yield condition, n priori, to the form of constant inplane principal shear stress near the crack tip are made, and the analysis is v...

A model has been developed to predict crack opening and closing behavior for propagating fatigue cracks which undergo significant sliding displacements at crack flanks. Crack surfaces were described statistically by assuming a random distribution of asperity heights and a mean density of asperities and asperity radii. The propagating crack was subdivided into strips, and each strip was treated ...

This paper investigates the phenomenon of slant fracture observed in stable tearing tests of many ductile materials, where an initially flat crack, loaded under remote Mode I conditions, tends to grow into a slant crack and stay in the slant configuration until final fracture. In an effort to identify potential reasons why cracks prefer to grow in a slant manner, three-dimensional finite elemen...

The tensile fractures of ultrafine-grained (UFG) Al-Mg alloy with a bimodal grain size were investigated at the microand macroscale using transmission electron microscopy (TEM), scanning electron microscopy (SEM) equipped with focused ion beam (FIB), and optical microscopy. The nanoscale voids and crack behaviors near the tensile fracture surfaces were revealed in various scale ranges and provi...