Cerium doped lutetium silicate powders were prepared by solegel process with different cerium concentrations (0, 0.01 and 0.03 mol%). The synthesized lutetium silicate powders were investigated by X-ray diffraction (XRD), TG-DTA, SEM, and Photoluminescence excitation and emissions. The crystallization of lutetium silicate is observed at 1.073 C in S2 (and S3: 1.058 C) sample. The formation of l...

Coatings prepared from nanosized powders were obtained by spraying ethanol-based colloidal solutions into a plasma plume. The powders investigated included 40 nm γ -Al2O3, 75 nm 8 wt% Y2O3-ZrO2, and 750 nm 25 wt% CeO2-ZrO2. Spray distances from approximately 50 to 63 mm were required to achieve significant coating deposition. As observed in the TEM, the typical lamella morphology of air plasma ...

The purpose of this research was to study the effect of doped Ag on phase transformation, morphology and photocatalytic activity of TiO2 powders. The composites powders were prepared by sol-gel method via calcinations at a temperature 400 °C for 2 h with a heating rate of 10 °C/min. The microstructure and crystallite size of TiO2 and TiO2-Ag powders were characterized by XRD, EDX and SEM. Final...

sol–gel auto-combustion is a unique combination of the combustion and the chemical gelation processes. in this work, nanosize (d) powders with compositions of znfe2o4 were synthesized by sol–gel combustion method. the puffy, porous brown powders as-combusted was calcined at the temperature of 750–1000◦c for 4 h. these powders are characterized by x-ray diffraction and scanning electron microsco...

The structural evolution of nanocrystalline TiO2 was studied by X-ray diffraction (XRD) and the Rietveld refinement method (RRM). TiO2 powders were prepared by the sol-gel technique. Post annealing of as-synthesized powders in the temperature range from 500 degrees C to 800 degrees C under air and argon atmospheres led to the formation of TiO2 nanoparticles with mean crystallite size in the ran...

Ultrafine MgH₂ nanocrystalline powders were prepared by reactive ball milling of elemental Mg powders after 200 h of high-energy ball milling under a hydrogen gas pressure of 50 bar. The as-prepared metal hydride powders were contaminated with 2.2 wt. % of FeCr-stainless steel that was introduced to the powders upon using stainless steel milling tools made of the same alloy. The as-synthesized ...

The effects of high pressure (HP) treatment (100-400 MPa at 10-60 °C) on the solubility of milk protein concentrate (MPC) powders were tested. The solubility, measured at 20 °C, of fresh MPC powders made with no HP treatment was 66%. It decreased by 10% when stored for 6 weeks at ambient temperature (~20 °C) and continued to decrease to less than 50% of its initial solubility after 12 months of...

The synthesis of pure and well dispersed lutetium aluminum garnet (LuAG) powder is crucial and important for the preparation of LuAG transparent ceramics. In this paper, high purity and well dispersed LuAG powders have been synthesized via co-precipitation method with lutetium nitrate and aluminum nitrate as raw materials. Ammonium hydrogen carbonate (AHC) was used as the precipitant. The influ...

The artichoke by-products from the canning industry are mainly used for silage, being minimally revaluated. The ways of extraction of by-products of artichoke into fiber-rich powders modify their industrial applications in biscuits, as the sensory evaluation may change compared with the reference fiber (Pea fiber, P) used with commercial biscuit. In this sensory study biscuits enriched with fib...

In this study, a novel self-assembling hydrogen generation powder comprised of 80Al-10Bi-10Sn wt.% was prepared using the gas atomization method and then collected in an air environment. The morphological and hydrolysis properties of the powders were investigated. The results indicated that the powders formed unique core/shell microstructures with cracked surfaces and (Bi, Sn)-rich phases distr...