Compositionally graded glass-filled epoxy sheets with edge cracks initially along the gradient are studied under dynamic loading conditions. Specimens with monotonically varying volume fraction of reinforcement are subjected to mixed-mode loading by eccentric impact relative to the crack plane. The optical method of Coherent Gradient Sensing and high-speed photography are used to map transient ...

In this work we describe a series of impact experiments performed on PMMA/4340 steel edge cracked bimaterial plates. Specimens were impacted at 20 m SK’ in a one point bend configuration using a high speed gas gun. Dynamic interfacial crack propagation was observed using the optical method of Coherent Gradient Sensing and high speed photography. Very high crack tip accelerations (IO’ m SF’) and...

Abstract. Eddy current testing using a pickup coil is usually applied to the surface detection of cracks because of its high frequency. However, for metal infrastructure, detection of not only the surface but also internal cracks is desired. Therefore, we have developed a low-frequency eddy current testing system to inspect interior structures using a magneto-resistive (MR) sensor with a wide m...

In this paper, the thermo-mechanical reliability of Cu/ultra low-k interconnects under chip to package interaction was investigated using finite element modeling and modified edge liftoff test (MELT). The crack propagation behavior in the low-k interconnect was simulated based on the crack tip opening displacement method (CTOD) and the maximum hoop stress criterion. In a six-level Cu/low-k inte...

The diffraction of SH waves by a finite plane crack is studied. The classical Sommerfeld solution for a semi-infinite straight reflecting screen is used as a building block to calculate the diffracted field generated by a finite crack. The solution is derived from the analysis of the behaviour of diffracted waves. These waves, which are first generated at the edges of the crack, travel along th...

In the current research work, the problem of fracture mechanics in a plate with a central hole under tensile loading is studied. The stress intensity factors are calculated for a finite plate containing two symmetrical hole-edge cracks. The problem is solved by two different methods, namely the finite element method and the FRANC software analysis. At first the finite element method is used and...

The resonance phenomenon observed in Rayleigh wave scattering from surface-breaking cracks has been investigated using Freund's results on reflection of Rayleigh waves from an infinite crack edge. To model the crack as a section of acoustic waveguide, resonances are treated as standing waves in the length and depth directions. The model takes both faces of the crack into consideration, and this...

Ceramic coatings deposited on metal substrates generally develop significant compressive stresses when cooled from the temperature at which they are processed as a result of thermal expansion mismatch. One of the main failure modes for these coatings is edge delamination. For an ideally brittle interface, the edge delamination of a compressed thin film involves mode II interface cracking. The c...

The work involves develops attended by a numerical execution of the eXtend Finite Element Method premises a measurement by the fracture process cracked so many cracked plates an application will be processed for the calculation of the stress intensity factor SIF. In the first we give in statically part the distribution of stress, displacement field and strain of composite plate in two cases unc...

Crack front waves are nonlinear localized waves that propagate along the leading edge of a crack. They are generated by both the interaction of a crack with a localized material inhomogeneity and the intrinsic formation of microbranches. Front waves are shown to transport energy, generate surface structure, and lead to localized velocity fluctuations. Their existence locally imparts inertia, wh...