This study investigates the influence of curing age and mix proportions on the compressive strength of volcanic ash (VA) blended cement laterized concrete. A total of 288 cubes of 100mm dimensions were cast and cured in water for 3, 7, 28, 56, 90 and 120 days of hydration with cement replacement by VA and sand replacement by laterite both ranging from 0 to 30% respectively while a control mix o...

We aimed to determine the optimal method of inserting a screw into polymethylmethacrylate (PMMA) cement to enhance fixation. We performed six groups of ten axial pull-out tests with two sizes of screw (3.5 and 4.5 mm AO cortical) and three methods of insertion. Screws were placed into 'fluid' PMMA, into 'solid' PMMA by drilling and tapping, or into 'curing' PMMA with quarter-revolution turns ev...

This paper aims to study the feasibility of highly conductive carbon fiber reinforced concrete (CFRC) as a self-heating material for ice formation prevention and curing in pavements. Tests were carried out in lab ambient conditions at different fixed voltages and then introduced in a freezer at -15 °C. The specimens inside the freezer were exposed to different fixed voltages when reaching +5 °C...

A model that describes hydration and heat-mass transport in Portland cement mortar during steam curing was developed. The hydration reactions are described by a maturity function that uses the equivalent age concept, coupled to a heat and mass balance. The thermal conductivity and specific heat of mortar with water-to-cement mass ratio of 0.30 was measured during hydration, using the Transient ...

Concrete is an essential building material which is widely used in construction industry all over the world due to its compressible strength. Curing of concrete plays a vital role in durability and other performance necessities. Improper curing can affect the concrete performance and durability easily. When areas like scarcity of water, structures is not accessible by humans external curing can...

OBJECTIVE The aim of this study was to determine the effects of light intensity and type of light unit (quartztungsten-halogen [QTH] or light-emitting diode [LED]) on the hardening of various resin cements and a resin composite restorative. METHODS Disk specimens were prepared from 4 dual-cured resin cements (Variolink II, Calibra, Nexus 2 and RelyX ARC). Two QTH light-curing units (Visilux 2...

OBJECTIVES The aim of this in vitro study was to evaluate the influence of different light curing units and modes on microleakage of flowable composite resins. METHODS Eighty Class V cavities were prepared in buccal and lingual surfaces of 40 extracted human premolars with cervical wall located in dentin and the occlusal wall in enamel. These teeth were randomly assigned into two groups (n=20...

A macroscopic compression test utilizing a simple custom-built instrument was employed to measure polydimethylsiloxane (PDMS) elastic modulus. PDMS samples with varying crosslinking density were prepared with the elastomer base to the curing agent ratio ranging from 5 : 1 to 33 : 1. The PDMS network elastic modulus varied linearly with the amount of crosslinker, ranging from 0.57 MPa to 3.7 MPa...

Soybean oil-based composites are prepared by the solid freeforming fabrication (SFF) method. Epoxidized soybean oil is solidified with a gelling agent, and composites are formed by fiber reinforcement. Glass, carbon, and mineral fibers are used in the formulations. The type of fiber and degree of fiber alignments affect the properties of the composites. In addition, the effects of curing agents...