The substrate material was nickel-based superalloy (In738LC), and CoNiCrAlY was pressureless plasma-sprayed on the substrate as the bond coating. As the top coating, zirconia with 4 mol% yttria was electron beam-physical vapor deposited (EB-PVD) on the rotating substrate. The rotation speeds in the EB-PVD process were 5, 10 and 20rpm. The specimens were exposed to 1273K in air atmosphere for 20...
In this study, the effect of surface morphologies on the isothermal oxidation behavior of MCrAlY coatings fabricated by high-velocity oxyfuel (HVOF) processes was investigated. To do so, free standing coatings with as-sprayed and polished surfaces were isothermally oxidized at 1050°C. The thickness of the bond coat was approximately 380μm. The Ra of the as-sprayed and polished surfaces were 6.4...
بهبود مقاومت به محیط کلسیم-منیزیم آلومینوسیلیکات (CMAS: CaO–MgO–Al2O3–SiO2) یکی از اهداف نوین و اصلی در صنایع توربینی و بهویژه در پوششهای سد حرارتی است. هدف از این تحقیق بهبود کیفیت و کارایی پوششهای سد حرارتی زیرکونیایی پایدار شده با ایتریا (YSZ) در محیط کلسیم-منیزیم آلومینوسیلیکات از طریق اعمال پوششهای دولایه با استفاده از زیرکونیای پایدار شده با سریا (CSZ)...
پوشش های روکشی به کار رفته در بخش های داغ توربین های گازی دارای مقاومت قابل قبولی در برابر خوردگی داغ هستند. با این وجود به دلیل مقدار آلومینیوم محدود آن ها، مقاومت به اکسیداسیون کمتری نسبت به پوشش های سنتی این قطعات یعنی پوششنفوذی آلومینایدی دارند. در پژوهش حاضر یک پوشش conicralyاعمال شده به روش پاشش پلاسمایی کم فشار تحت عملیات آلومینیوم دهی نفوذیبا دو شیوه رشد متفاوت برونگرا و درونگرا قرار گر...
نمودار تعداد نتایج جستجو در هر سال
با کلیک روی نمودار نتایج را به سال انتشار فیلتر کنید