In this study, two types of porous zirconia and dense zirconia were used. The flexural strength of non-layered zirconia specimens and those of the layered zirconia specimens with veneering porcelain were examined. Furthermore, the shear bond strength of veneering porcelain to zirconia was examined. The flexural strength of the non-layered specimens was 1,220 MPa for dense zirconia and 220 to 30...

D6056 prefabricated abutment includes placement D6057 custom abutment includes placement D6058 abutment supported porcelain/ceramic crown D6059 abutment supported porcelain fused to metal crown (high noble metal) D6060 abutment supported porcelain fused to metal crown (predominantly base metal) D6061 abutment supported porcelain fused to metal crown (noble metal) D6062 abutment supported cast m...

Laminate veneers are a conservative treatment of unaesthetic anterior teeth. The continued development of dental ceramics offers clinicians many options for creating highly aesthetic and functional porcelain veneers. This evolution of materials, ceramics, and adhesive systems permits improvement of the aesthetic of the smile and the self-esteem of the patient. Clinicians should understand the l...

Plasma and halogen lamp units were used to photo-cure a composite resin for porcelain bonding. Mean shear bond strengths to dentin after light curing through porcelain of 1 and 2 mm thickness ranged from 20 to 27 MPa before and after thermocycling, indicating no significant effects due to porcelain thickness, curing method, or thermocycling, except for plasma curing for 3 s through porcelain of...

STATEMENT OF PROBLEM Bonded porcelain veneers are widely used esthetic restorations. Although high success and survival rates have been reported, failures occur. Fracture is the most common failure mode. Fractures range from incomplete cracks to the catastrophic. Minimally invasive or thin partial veneers have gained popularity. PURPOSE The aim of this study was to measure the influences of p...

BACKGROUND This study evaluated the feasibility of fabricating implant abutments and crowns from pre-sintered feldspathic porcelain blocks using the chair-side CAD/CAM, CEREC3D((R)) system. METHODS Thirty-two implant analogues were divided into two groups. In the control group, prefabricated machined anatomical titanium (Ti) abutments were screw-retained to the analogues. In the test group, m...

This investigation examined the marginal characteristics of the collarless metal ceramic restoration made with two commonly used direct-lift techniques: (1) a porcelain/wax paste and (2) a porcelain/liquid slurry. The metal copings touched the shoulder in half of the groups and were left 0.5 mm short in the other half to comprise the four experimental groups. Marginal seal was evaluated at faci...

PURPOSE This study evaluated the bond strength between porcelain denture teeth (Bioblend 43D) and four different polymerized denture resins (Lucitone 199, Palapress, Acron MC, Triad) with and without a bonding agent and after four different types of surface treatment (polished, HF etched, sandblasted, air-abraded). MATERIALS AND METHODS Central incisor porcelain denture teeth were divided int...

OBJECTIVES The purpose of this study was to evaluate the effect of hot pressing on the shear bond strength of a Au-Pt-Pd alloy-porcelain composite. METHODS Several metal-porcelain composites specimens were produced by two different routes: conventional porcelain fused to metal (PFM) and hot pressing. In the latter case, porcelain was hot pressed onto a polished surface (PPPS) as well as a rou...

The need of taxonomy is vital for knowledge sharing. This need has been portrayed by through-life engineering services/systems. This paper addresses this issue by repair process taxonomy development. Framework for repair process taxonomy was developed followed by its implementation. The importance of repair process taxonomy has been highlighted.