An investigation of how microstructural features affect the fracture and fatigue properties of a promising class of high temperature Mo-Si-B based alloys is presented. Fracture toughness and fatigue-crack growth properties are measured at 25o and 1300oC for five Mo-Mo3Si-Mo5SiB2 containing alloys produced by powder metallurgy with α-Mo matrices. Results are compared with previous studies on int...

The application of intermetallic compounds for understanding in heterogeneous catalysis developed in an excellent way during the last decade. This review provides an overview of concepts and developments revealing the potential of intermetallic compounds in fundamental as well as applied catalysis research. Intermetallic compounds may be considered as platform materials to address current and f...

The Rietveld Method was used to investigate the structure of three Fe-Zn intermetallic phases and to quantify their proportion. The zeta, delta and gamma phases were successfully obtained by the sintering process. A simple mixture of the three intermetallic phases was made with a known mass percentage and the XRD pattern of this mixture was collected and analyzed by the Rietveld Method. A diffe...

An experiment on the early stages of intermetallic compound layer growth during soldering and its theoretical analysis were conducted with the intent to study the controlling factors of the process. An experimental technique based on fast dipping and pulling of a copper coupon in liquid solder followed by optical microscopy allowed the authors to study the temporal behavior of the sample on a s...

The present study demonstrates the evolution of eutectic microstructure in arc-melted (Zr0.76Fe0.24)100-xNbx (0 ≤ x ≤ 10 atom %) composites containing α-Zr//FeZr₂ nano-lamellae phases along with pro-eutectic Zr-rich intermetallic phase. The effects of Nb addition on the microstructural evolution and mechanical properties under compression, bulk hardness, elastic modulus, and indentation fractur...

This paper presents the results of studies on the influence of oxygen partial pressure (vacuum level in the chamber) on the properties of FeAl intermetallics. One of the problems in the application of classical methods of prepared Fe-Al intermetallic is the occurrence of oxides. Applying a vacuum during sintering should reduce this effect. In order to analyze the effect of oxygen partial pressu...

Erratum: Griffiths phase behaviour in a frustrated antiferromagnetic intermetallic compound Krishanu Ghosh, Chandan Mazumdar, R. Ranganathan & S. Mukherjee Scientific Reports 5:15801; doi: 10.1038/srep15801; published online 30 October 2015; updated on 02 February 2016 This Article contains errors in Figure 4 and Figure 5. In Figure 4, the y-axis ‘M (μ B/f.u.)’ was incorrectly given as ‘M(·B/f....

The rare coexistence of a Griffiths phase (GP) and a geometrically frustrated antiferromagnetism in the non-stoichiometric intermetallic compound GdFe0.17Sn2 (the paramagnetic Weiss temperature θp ~ -59 K) is reported in this work. The compound forms in the Cmcm space group with large structural anisotropy (b/c ~ 4). Interestingly, all the atoms in the unit cell possess the same point group sym...

The binary intermetallic clathrates K8-xSi46 (x = 0.4; 1.2), Rb6.2Si46, Rb11.5Si136 and Cs7.8Si136 were prepared from M₄Si₄ (M = K, Rb, Cs) precursors by spark-plasma route (SPS) and structurally characterized by Rietveld refinement of PXRD data. The clathrate-II phase Rb11.5Si136 was synthesized for the first time. Partial crystallographic site occupancy of the alkali metals, particularly for ...

Nickel and aluminum powders were mechanically alloyed with 10 or 30 vol.% refractory metal powders (molybdenum or tungsten) for times up to 50 h. Intermetallic synthesis takes place after lo-20 h alloying, with concomitant dispersion of the inert refractory metal phase, resulting in an NiAl matrix containing fine refractory dispersoids. The reactive synthesis step is direct, without intermediat...