The role of metal layer thickness and resultant plastic constraint in the metal layer during the failure of metal/ceramic layered structures is examined under cyclic and static loading conditions. Crack-growth experiments were conducted on sandwich specimens consisting of 99.999% pure aluminum layers bonded between 99.5% pure polycrystalline alumina with the metal layer thickness varying from 5...

Following our innovative experimental spontaneous fracture models for frictional fractures (compression and shear) and mixed-mode fractures (tension and shear) in identical materials, we designed a laboratory model to investigate the effects of material contrast on mixed-mode spontaneous fracture along a bimate-rial interface. A series of interesting phenomena are observed, including asymmetry ...

Based on the theory of elasticity, previous analytical solutions concerning a penny-shaped interface crack employ the derivative of the crack surface opening displacements as the primary unknowns, thus leading to singular integral equations with Cauchy-type singularity. The solutions to the resulting integral equations permit only the determination of stress intensity factors and energy release...

The shear lag model has been used in conjunction with the 3D elasticity equations to determine the stress state in a fiber/matrix system containing an interface crack. The use of a shear lag model to capture the stress state at the crack tip and the modelling of the region away from the crack tip by the elasticity equations leads to a simple analytical expression which can be used to determine ...

For a crack impinging upon a bimaterial interface at an angle, the singular stress field is a linear superposition of two modes, usually of unequal exponents, either a pair of complex conjugates, or two unequal real numbers. In the latter case, a stronger and a weaker singularity coexist (known as split singularities). We define a dimensionless parameter, called the local mode mixity, to charac...

Interface and interfacial cracks interacting with screw dislocations in piezoelectric bimaterials subjected to antiplane mechanical and in-plane electrical loadings are studied within the framework of linear piezoelectricity theory. Straight dislocations with the Burgers vector normal to the isotropic basal plane near the interface or interfacial crack are considered. The dislocations are chara...

Mixed-mode fracture of an adhesively-bonded structure made from a commercial adhesive and a dual-phase steel has been studied under different rates. Since mixedmode fracture occurs along the interface between the steel and adhesive, the cohesiveparameters for the interface were required. The mode-II interfacial properties were deduced in earlier work. In this paper the mode-I interfacial toughn...

The bonding strength between dissimilar materials in composites is often relatively weak. Interface debonding and cracking are of common occurrence. As an e€ ective method to minimize such failures, ® bre stitching is used to enhance the bonding strength when joining layers in polymer composites. With the presence of the reinforcing ® bre, the overall elastic response for each component of the ...

Effects of matrix cracks and the attendant interface debonding and sliding on both the longitudinal and the transverse thermal diffusivities of a unidirectional Nicalon/MAS composite are investigated. The diffusivity measurements are made in situ during tensile testing using a phase-sensitive photothermal technique. The contribution to the longitudinal thermal resistance from each of the cracks...