Experimentally determined T ε and CTOA resistance curves were used to simulate numerically, stable crack growth and the ensuing crack linkup in 0.8 mm thick 2024-T3 aluminum tension specimen with multiple site damage (MSD) subjected to monotonically/cyclically increasing loading. The T ε integral correctly predicted the crack growth and linkup history as well as the onset of rapid fracture in M...

This study presents a probabilistic, 3-D framework to describe brittle fracture in structural components which incorporates weakest link statistics and a micromechanics model reflecting local damage of material. The Weibull stress (a,) emerges as a fracture parameter to define conditions leading to local material failure. This parameter is correlated with the macroscopic loading and used to des...

BACKGROUND AND PURPOSE Growth factors released from platelets have potent effects on fracture and wound healing. The acidic tide of wound healing, i.e. the pH within wounds and fractures, changes from acidic pH to neutral and alkaline pH as the healing process progresses. We investigated the influence of pH on lysed platelet concentrates regarding the release of growth factors. MATERIAL AND M...

The topology of two discrete fracture network models is compared to investigate the impact of constrained fracture growth. In the Poissonian discrete fracture network model the fractures are assigned length, position and orientation independent of all other fractures, while in the mechanical discrete fracture network model the fractures grow and the growth can be limited by the presence of othe...

In this paper, the fatigue and fracture properties of bovine dentin are evaluated using in vitro experimental analyses. Double cantilever beam (DCB) specimens were prepared from bovine maxillary molars and subjected to zeroto-tension cyclic loads. The fatigue crack growth rate was evaluated as a function of the dentin tubule orientation using the Paris law. Wedge-loaded DCB specimens were also ...

An understanding of the evolution of toughness is essential for the mechanistic interpretation of the fracture of cortical bone. In the present study, in vitro fracture experiments were conducted on human cortical bone in order to identify and quantitatively assess the salient toughening mechanisms. The fracture toughness was found to rise linearly with crack extension (i.e., rising resistance-...

initial cracks occur in high strength concrete sleepers for various reasons, such as shrinkage and wrong curing and long lifetime of over 50 years of sleepers. these cracks may lead to complete failure of the structure. in order to more accurately design the sleepers, fracture mechanics (not strength of materials) should be incorporated. in order to achieve this purpose, it is important to fore...

Maleic anhydride-modified polypropylene was compounded with commercially available surface-modified montmorillonite in a twin-screw extruder. Recompounding ensured the removal of visible tactoids from the extrudate but TEM and XRD techniques showed nonuniform dispersion of clay platelets. In this study, we investigated the mechanical and fracture properties of nanoclayfilled polypropylene. Emph...

Fracture toughness tests were conducted for an A533B-1 steel by using chevron-notched compact specimens in the temperature range from the lower shelf regime up to the transition temperature in order to assess the R-curve for cleavage fracture. The applicability of these specimens to the simple fracture toughness test without introducing fatigue pre-cracks was examind. The following are the summ...

The lipid phase of cytoplasmic membrane was studied by freeze-fracture electron microscopy in the chilling-susceptible blue-green alga, Anacystis nidulans. At growth temperatures, intramembrane particles were distributed at random in the fracture faces of cytoplasmic membrane, whereas, at chilling temperatures, the fracture faces were composed of particle-free and particle-containing regions. T...