The process of ductile fracture which occurs due to the accumulation, growth and combination of defects or cracks of material is called ductile damage. Failure in materials can be predicted, using damage mechanics and damage criteria. On the other hand, most of the materials depended to the manufacturing process, are formed in warm or hot conditions so that; the temperature also affects on the ...

This paper presents an investigation of the mechanism of the brittle–ductile cutting mode transition from the perspective of the mechanics. A mechanistic model is proposed to analyze the relationship between undeformed chip thickness, deformation, and stress levels in the elastic stage of the periodic chip formation process, regarding whether brittle or ductile mode deformation is to follow the...

Tensile test on smooth and circumferentially notched specimens, systematic observation of fracture surfaces and large deformation finite element analysis were conducted to understand the deformation and failure behavior of a magnesium alloy (AM60). The plastic deformation is considered to be dominated by twining mediated slip. The tensile properties were not sensitive to the strain rates applie...

A unified experimental-computational study on ductile fracture initiation and propagation during small punch testing is presented. Tests are carried out at room temperature with unnotched disks of different thicknesses where large-scale yielding prevails. In thinner specimens, the fracture occurs with severe necking under membrane tension, whereas for thicker ones a through thickness shearing m...