Due to the broad applications of porous alumina nanostructures, research on fabrication of anodized aluminum oxide (AAO) with nanoporous structure has triggered enormous attention. While fabrication of highly ordered nanoporous AAO with tunable geometric features has been widely reported, it is known that its growth rate can be easily affected by the fluctuation of process conditions such as ac...

The anodization of aluminum is an electro-chemical process that changes the surface chemistry of the metal, via oxidation, to produce an anodic oxide layer. During this process a self organized, highly ordered array of cylindrical shaped pores can be produced with controllable pore diameters, periodicity and density distribution. This enables anodic aluminum oxide (AAO) membranes to be used as ...

A new pressure measurement technique for measuring the pressure over rotating blades of industrial axial flow fan is described in this paper. The new technique is called pressure sensitive foil (PS-Foil) technique. In this technique a very thin aluminum foil is coated with pressure sensitive paint using anodization method. The resulting PS-Foil can be stick over any existing blade using a very ...

To improve the photo-catalytic degradation of salicylic acid, we reported the fabrication of ordered TiO2 nanotube arrays by a simple and effective two-step anodization method and then these TiO2 nanotubes treated in a methanol solution under UV light irradiation. The TiO2 nanotubes prepared in the two-step anodization process showed better photo-catalytic activity than TiO2 nanotubes prepared ...

A high-throughput process for nanotexturing of hard and soft surfaces based on the roll-to-roll anodization and etching of low-cost aluminum foils is presented. The process enables the precise control of surface topography, feature size, and shape over large areas thereby presenting a highly versatile platform for fabricating substrates with user-defined, functional performance. Specifically, t...

Practical application of superhydrophobic surfaces is limited by the fragility of nanoscale asperities. Combining chemical etching and anodization, microscale pits and nanoscale pores, instead of the micro and nano protrusions on traditional superhydrophobic surfaces mimicking Lutos leaves, were fabricated on commercially pure aluminum surfaces. After modified by FDTS, the surfaces were superhy...

The foils laminate approach can be implemented to grow bi-directional porous pattern from both the top and bottom surfaces of an aluminum foil. It was intuitively inferred that leakage of etchant from the clamped area can be a feasible cause to have the upward pores grow in the notches of the unpolished surface. This leakage hypothesis has been disproved by the leakage blocking and triple layer...

Arrays of ideally ordered alumina nanochannels with unprecedented ,10 nm pore size, 40–50 nm interpore spacing, and improved channel uniformity have been fabricated by anodizing an aluminum substrate with a guiding pattern on its surface. The pattern is an array of hexagonally close-packed concaves fabricated by focused ion beam direct sputtering; and its lattice constant is carefully matched t...

To improve the photo-catalytic degradation of salicylic acid, we reported the fabrication of ordered TiO2 nanotube arrays by a simple and effective two-step anodization method and then these TiO2 nanotubes were treated in a methanol solution under UV light irradiation. The TiO2 nanotubes prepared in the two-step anodization process showed better photo-catalytic activity than those prepared in o...