The present paper is concerned with the application of a “plasticity-induced” crack closure model to study fatigue crack growth under various load histories. The model was based on the Dugdale model but modified to leave plastically deformed material in the wake of the advancing crack. The model was used to correlate crack growth rates under constant-amplitude loading and then used to predict c...

initial cracks occur in high strength concrete sleepers for various reasons, such as shrinkage and wrong curing and long lifetime of over 50 years of sleepers. these cracks may lead to complete failure of the structure. in order to more accurately design the sleepers, fracture mechanics (not strength of materials) should be incorporated. in order to achieve this purpose, it is important to fore...

BACKGROUND Slow crack growth can be described in a v (crack velocity) versus KI (stress intensity factor) diagram. Slow crack growth in ceramics is attributed to corrosion assisted stress at the crack tip or at any pre-existing defect in the ceramic. The combined effect of high stresses at the crack tip and the presence of water or body fluid molecules (reducing surface energy at the crack tip)...

Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF) evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-is...

Fatigue crack growth (FCG) rates have previously been reported in forged Ti6Al-4V aero-engine disk material under the conjoint action of LCF and HCF cycles at room temperature. It is found that systematic increases in LCF overload, applied prior to the commencement of the HCF cycles, reduce the contribution of the HCF cycles to crack growth rates. The application of overload also enhances the s...

Fatigue cracking is one of the most common failure modes of various load-bearing structures. Even though sensors of many different types have been developed for crack detection, very few can monitor crack growth with a high sensitivity. This paper presents an antenna sensor that is capable of monitoring the growth of fatigue cracks with a sub-millimeter resolution. According to microstrip patch...

Stable ductile crack growth in 3 mm thick AISI 304 stainless steel specimens has been investigated experimentally and numerically. Multi-linear Isotropic Hardening method coupled with the Von-Mises yield criterion was adopted for modeling elasto-plastic behavior of the material. Mode-I CT fracture specimens have been tested to generate experimental load-displacement-crack growth data during sta...

In situ ultrasonic fatigue with a cyclic frequency of 20 kHz was employed in an environmental scanning electron microscope (ESEM) to characterize fatigue crack formation and growth in the near alpha titanium alloy Ti–6242S. The role of environment on small fatigue crack initiation and growth was investigated in vacuum and in variable pressures of saturated water vapor, as well as in laboratory ...

In the present work, interactions between a macro-crack and various micro-crack configurations are studied extensively. Influence of different on propagation main crack is numerically examined by ordinary state-based peridynamics. Certain improve toughness specimens, while some only has marginal impact growth rate. Furthermore, very complex patterns effectively simulated implementation formulat...

Title: Crack Growth During Brittle Fracture in Compression. Author: Bartlett W. Paulding, Jr. Submitted to the Department of Geology and Geophysics February 9, 1965 in partial fulfillment of the requirements for the degree of Doctor of Philosophy at the Massachusetts Institute of Technology. Photoelastic analysis of several two-crack arrays predicts that compressive fracture is initiated at cra...