The development of different materials for the use in posterior areas for aesthetic monolitic crowns has been a challenge in dental technology. The goal of this study was to develop 3D posterior teeth covered with complete aesthetic monolitic crowns and to compare the stress distributions under loads, revealing the effect of various materials on the biomechanical performance of the crowns. For ...

Early types of metal-free ceramics did not enjoy success in dentistry, especially in the posterior region (Shimada et al., 2002). The high crystalline content ceramic systems have been developed in an attempt to improve the strength of metal-free restorations as well as deliver more esthetic results than conventional metal-fused-to-ceramic restorations (Ozcan et al., 2001; Valandro et al., 2006...

OBJECTIVE To evaluate the marginal gap (MG) and absolute marginal discrepancy (MD) of full ceramic crowns with two finish line designs, shoulder and chamfer, using microcomputed tomography (micro-CT) before and after cementation. MATERIALS AND METHODS Sixty extracted human maxillary premolar teeth were divided into two groups based on the finish line design: Group I: 90° shoulder and Group II...

OBJECTIVES To assess the effect of interfacial surface roughness on the flexure strength and fracture mode and origin utilizing an in-vitro assessment of the clinical failure conditions expected for all-ceramic crowns and the connector area of fixed partial dentures (FPDs) using bilayered ceramic specimens tested in bi-axial flexure. METHODS Sets of 20 bilayered composite discs, with core:den...

Fracture of ceramic materials has been one of the most frequently reported complications for all-ceramic restorations. The aim of the study was to analyze the fracture features of hot-pressed ceramic crowns in order to evaluate areas susceptible to crack initiation and crack propagation correlated with stress areas. The crowns were inspected visually to determine the shape and orientation of th...

background and aim: metal ceramic restorations are widely used in crowns. the marginal fitness of these artificial crowns is prone to alteration during the firing cycle of porcelain. gold electroformed metal-ceramic restorations have been introduced as alternatives to conventional metal-ceramic restorations. however little is known about the relationship between procelain firing procedures and ...

STATEMENT OF PROBLEM The influence of different crown foundations on marginal seal and fracture resistance of ceramic crowns placed on endodontically treated teeth has not been clearly established. PURPOSE The purpose of this study was to evaluate the marginal continuity and fracture behavior of high-strength all-ceramic crowns with different substructures in endodontically treated premolars....

The scope of the study was a retrospective evaluation, involving a 1‐3 year follow‐up period, of the periodontal condition of teeth with fixed crowns. The experimental group was formed of 40 patients having followed a prosthetic treatment with ceramic crowns. The complete clinical evaluations performed included analysis of the plaque index (IP), of the index of gingival bleeding (ISG), probing ...

OBJECTIVE The purpose of this study was to determine the effect of two extraoral computer-aided design (CAD) and computer-aided manufacturing (CAM) systems, in comparison with conventional techniques, on the marginal fit of monolithic CAD/CAM lithium disilicate ceramic crowns. STUDY DESIGN This is an in vitro interventional study. PLACE AND DURATION OF STUDY The study was carried out at the...