Calcium aluminate cement (CAC) suffers from loss of workability in less than an hour (~15 minutes) after first touch of water. Current superplasticizers that are utilized to modify the viscosity of cement admixtures are designed to target ordinary Portland cement (OPC). The high affinity between these superplasticizers and cement particles were found to be detrimental in CAC systems. Utilizatio...

The effect of using Na2HPO4 solution as mixing liquid in the physicochemical and mechanical properties of calcium aluminate cement (CAC), with a view to a possible reinforcement additive of conventional α-TCP-based CPC was studied. The results showed that the degree of the hydration reaction of CaAl2O4 (CA) increased when Na2HPO4 solution was used as mixing liquid. The porosity of cement was al...

In this study, the evaluation of aluminium dross from secondary production in calcium aluminate cement was investigated. Salt compounds were removed significantly by washing. Mixtures washed and quicklime prepared to obtain a additive considering standard with low alumina they sintered at 1250 °C for 5 h. The phases mayenite, monocalcium aluminate, grossite, gehlenite, larnite, periclase spinel...

Hydration products of calcium silicates and calcium aluminates often are difficult to identify by X-ray methods. In this study the hydration products of the aluminate phase especially under the influence of additional chloride ions were studied. Special X-ray measurement conditions must be applied for accurate identification including 1. In situ control of relative humidity 2. Exclusion of CO2 ...

in this work, we studied the effect of carboxylic acid on the rheological properties of a high-alumina cement mortar (ch45) produced by the algerian firm refractal.the investigated properties are setting time, water consumption, electrical conductivity, ph, density and the compressive strength. the results show a setting time of about 200 min for the acid free, 180 min with 0.1 % of carboxylic ...

J. Burja, F. Tehovnik, F. Vode, B. Arh, Institute of Metals and Technology, Ljubljana, Slovenia In this chromium slags that form during melting of chromium alloyed steels are examined. During melting and oxidation of these steel grades a considerable amount of chromium is lost, and gained back with slag reduction. Laboratory experiments were performed to study the mechanism of chromium oxide re...

It is necessary to elucidate the crystallization thermodynamic of mineralogical phases during the cooling process of the molten BFS with different chemical composition, because the high-melting point mineral phase maybe crystallized during the fiber forming and thereafter cooling process. Thermodynamic calculation software FactSage6.4 and the hot remelting experiments were performed to explore ...