The electrochemical and corrosion behavior of a stainless-steel-based alloy made as a prototype metallic nuclear wasteform to immobilize Tc, has been studied in a number of reference solutions ranging in pH from 4 to 10. The results showed the 47SS(304)-9Zr–23Mo prototype alloy contained at least five distinct phases with the majority of the Re, used as a Tc surrogate, contained within a Fe2Mo ...

This paper presents positron lifetime studies of the subsurface region of AK12 aluminium alloy and Al2O3-particle-reinforced AK12 aluminium alloy composite after sliding against steel in the pin-on-disc machine. The defect depth profile detected in the AK12 alloy extended up to 300 μm but for the composite AK12 the range of this profile was significantly shortened to less than ∼ 90 μm. The posi...

The effect on Fe-Cr phase separation of a uniaxial stress during thermal ageing at 425 °C is investigated on a Fe-15Cr-5Ni steel, a model alloy of commercial 15-5 PH steel. The applied stress is shown to accelerate the ageing kinetics, and influence the morphology of Cr rich domains. A dependence of the phase separation decomposition kinetics on the relative orientations of the load and the cry...

A need t o find a suitable replacement for cadmium electroplated coatings on mediumto highstrength steels has accelerated the development of economically viable alternatives. This edited version of a presentation at the 30th annual AerospaceIAirline Plating & Metal Finishing Forum examines the development of Australia's Defence Science and Technology Organisation's (DSTO) zinc-nickel electropla...

A duplex microstructure consisting of allotriomorphic ferrite and austenite at ambient temperature, has been produced in a low–alloy steel, by a simple heat treatment which involves intercritical annealing followed by quenching. The tensile properties obtained are good, with a total elongation of some 28% at an ultimate tensile strength approaching 900MPa. The form of the stress versus strain c...

This study was conducted to evaluate the biocompatibility of titanium-nickel shape memory alloy used as a medical implant material. The authors carried out the following electrochemical corrosion test and in vivo and in vitro biological tests for the alloy and some metal and alloys clinically used previously to compare the intensities concerned with the biological reactions, that is, (1) anodic...

In this paper, the fractal dimensions are proposed for characterizing the optical fiber corrosion sensors, which is applied to measure the steel corrosion based on Fe-C alloy film. Because corrosion was a complex random phenomenon and the corrosion surface of Fe-C alloy film of the optical fiber corrosion sensor possessed fractal characteristics, the image fractal dimensions is as a quantitativ...

Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...

Libya is an important oil country particularly to European countries. The combustion products of fossil fuels are causing great damage through pollution, acid rains and the greenhouse effect. Hydrogen can be stored in three different ways, as a gas, as liquid, as a material and metal hydrides. Low alloy steels have been widely used in different scale welded structures. The mechanical properties...

Reports of differing failure rates of total hip prostheses made of various metals prompted us to measure the size of metallic and polyethylene particulate debris around failed cemented arthroplasties. We used an isolation method, in which metallic debris was extracted from the tissues, and a non-isolation method of routine preparation for light and electron microscopy. Specimens were taken from...