We report on the formation of organized sub-micron YBa(2)Cu(3)O(7) (YBCO) dots induced by irradiating femtosecond laser pulses on YBCO films prepared by pulse laser deposition with fluence in the range of 0.21 approximately 0.53 J/cm(2). The morphology of the YBCO film surface depends strongly on the laser fluences irradiated. At lower laser fluence (approximately 0.21 J/cm(2)) the morphology w...

We describe the development of high-T e Josephson junction devices for applications at millimeter wave frequencies. These devices consist of ramp type YBCO/PBCO/YBCO Josephson junctions that are equipped with a noble metal log-periodic antenna. Growth conditions of all layers, as well as etching, cleaning and annealing procedures are being optimized, to guarantee well-defined device properties....

For a systematic study of energy relaxation processes in thin NbN and YBCO films on sapphire substrates, a frequency domain technique has been set up and employed. The magnetron sputtered NbN films of 3 nm to 22 nm thickness and pulsed-laser deposited YBCO films with thicknesses between 20 nm and 45 nm were excited by amplitude-modulated optical radiation (λ = 850 nm). The response spectra were...

High T, superconducting YBazCusO, (YBCO) thin films have been prepared on (305) SrTiOs (STO) substrates. X-ray diffraction analysis and Rutherford backscattering experiments reveal that the c-axis of the layers is directed along the [OOl] ST0 axis. Bragg reflection measurements from YBCO lattice planes with high h, k, and I indices confirm that the film growth is epitaxial and almost single dom...

We present a comprehensive study of the light-induced transient nonequilibrium kinetic inductive response of high-quality, epitaxial Y–Ba–Cu–O (YBCO) thin films. The test structures consisted of 20–30 μm wide coplanar strip (CPS) transmission lines with 7–10 μm separation, patterned in 100 nm thick YBCO films grown on MgO and LaAlO3 substrates. Each CPS structure contained a 5 μm wide, 7–10 μm ...

We examine the anomalous inverse spin switch behavior in La0.7Ca0.3MnO3(LCMO)/YBa2Cu3O7-δ (YBCO)/LCMO trilayers by combined transport studies and polarized neutron reflectometry. Measuring magnetization profiles and magnetoresistance in an in-plane rotating magnetic field, we prove that, contrary to many accepted theoretical scenarios, the relative orientation between the two LCMO's magnetizati...

A scanning transmission electron microscope (STEM) is used to examine the structural and chemical quality of the interface between thin films of YBa2Cu3O72d (YBCO) and BaF2. The STEM images indicate that it is possible to grow a uniform thin film of BaF2 that is relatively free of gross defects via a thermal evaporation method on top of a YBCO thin film. The diffraction contrast results also su...