Environmental pollution from human and industrial activities has received much attention as it adversely affects human health and bio-diversity. In this work we report efficient visible light photocatalytic degradation of phenol using supported zinc oxide (ZnO) nanorods and explore the role of surface defects in ZnO on the visible light photocatalytic activity. ZnO nanorods were synthesized on ...

The fabrication of galactose biosensor based on functionalised ZnO nanorods is described. The galactose biosensor was developed by immobilizing galactose oxidase on ZnO nanorods in conjunction with glutaraldehyde as a cross-linker molecule. The IRAS study provided evidence for the interaction of galactose oxidase with the surface of ZnO nanorods. The electromotive force (EMF) response of the ga...

Hydrothermally grown ZnO nanorods have inherent crystalline defects primarily due to oxygen vacancies that enhance optical absorption in the visible spectrum, opening up possibilities for visible light photocatalysis. Comparison of photocatalytic activity of ZnO nanorods and nanoparticle films on a test contaminant methylene blue with visible light irradiation at 72 kilolux (klx) showed that Zn...

ZnO nanorods were grown on a silver-coated tip of a borosilicate glass capillary (0.7 μm in tip diameter) and used as selective potentiometric sensor of intracellular free Mg(2+). To functionalize the ZnO nanorods for selectivity of Mg(2+), a polymeric membrane with Mg(2+)-selective ionophores were coated on the surface of the ZnO nanorods. These functionalized ZnO nanorods exhibited a Mg(2+)-d...

In the present work, novel nanotool called 'nano-embedded fungus' formed by impact of synergistic association of ZnO-nanorods and fungus Piriformospora indica DSM 11827, for growth of Brassica oleracea var. botrytis (Broccoli) is reported. ZnO-nanorods were synthesized by mechanical assisted thermal decomposition process and characterized by scanning electron microscopy (SEM) for morphology, X-...

We investigated the local structural properties of ZnO nanoparticles (NPs), nanorods and powder by using extended X-ray absorption ne structure (EXAFS). The average diameter and size of the ZnO NPs and nanorods were about 4.5 nm and 40 nm, respectively. The EXAFS analysis revealed that the bonding lengths of atoms in the ZnO nanorods were slightly elongated along the c-axis while they were shru...

Single crystal ZnO nanotube arrays were synthesized at low temperature in an aqueous solution containing zinc nitrate and hexamethylenetetramine. It was found that the pH value of the reaction solution played an important role in mediating the growth of ZnO nanostructures. A change in the growth temperature might change the pH value of the solution and bring about the structure conversion of Zn...

Cu2O-modified ZnO nanorods are prepared by a two-step electrodeposition method on ITO substrates, and the deposition time of Cu2O is 0, 1, 5, and 10 min, respectively. Cu2O particles are embedded in the interspaces of the ZnO nanorods, and the amounts of the Cu2O particles increase obviously when the deposition time lasts longer. The peaks corresponding to ZnO nanorods and Cu2O particles are de...

One-dimensional nanorods open up many new device applications. As one of the semiconductor nanorods, ZnO-based nanorods have been studied for electronic and photonic nanodevice applications. Recently, we developed catalyst-free metal-organic chemical vapor deposition of ZnO nanorods and employed these ZnO nanorods for electrical and optical nanodevice applications. In this presentation, I will ...

ZnO nanorods (diameters∼25 nmand lengths∼145-150 nm) were synthesized by using a simple solochemical method and their LPG sensing properties were investigated. The ZnO nanorods exhibited outstanding gas sensingcharacteristics such as, higher gas response (∼502 to 50ppm LPG at 300 ◦C), extremely rapid response(∼6-7 s), fast recovery (∼6–7 s), excellent reproducibility, good sensing selectivity a...