In cold rolling of thin strips, i.e., foils (Thickness

 One of the surface defects that arise in sheet metal working is when the part removes from the die. Since there are no external forces to make this defect, the origin of such fail is known as residual stress. Residual stress can develop in sheet metal forming due to non uniform deformation. In this paper, the workpiece is carbon steel with different volume fractions and arrangement of ferrite ...

Prediction of the mechanical behavior of thin foils (~25 µm) requires special characterization techniques. The current work is focused on the mechanical and microstructural characterization of 25 µm HAVAR alloy foils following annealing, cold rolling, and subsequent heat treatments, using small punch testing (SPT), X-ray diffraction (XRD), and transmission-scanning electron microscopy (TEM). Th...

in this study, the effects cold rolling and annealing parameters during thermomechanical processing of the aisi 201ln stainless steel were investigated. the cast samples were homogenized, hot-rolled and solution-annealed to acquire a suitable microstructure for the subsequent thermomechanical treatment. unidirectional and transverse multi-pass cold rolling at 25, 0 and -15 °c was carried out to...

in this article, the experiments carried out on making, rolling and measuring the physical and mechanical properties of iow - carbon ferritic steels of various phosphorus contents ranging from 0.0 11 to 0.085 percent are discussed • the results indicate that possibility of performance of both cold and hot rolling operations up to at least one fourth of the initial thickness exists through a seq...

in this study, the effects of nitrogen addition on the production of ultrafine/nano grained aisi 201l stainlesssteel by advanced thermo-mechanical process were investigated. cast samples were first homogenized at 1200 °c for 4 h, hot-rolled at 1100 °c and finally, solution-annealed at 1150 °c for 2.5 h. unidirectional and cross multipass cold rolling at 25 °c was carried out to 90% reduction in...

In this study, the effects of nitrogen addition on the production of ultrafine/nano grained AISI 201L stainless steel by advanced thermo-mechanical process were investigated. Cast samples were first homogenized at 1200 °C for 4 h, hot-rolled at 1100 °C and finally, solution-annealed at 1150 °C for 2.5 h. Unidirectional and cross multipass cold rolling at 25 °C was carried out to 90% reduction i...