The aim of this study was to investigate the possible reinforcement of Nanodiamonds (ND) in a PMMA resin for fixed interim restorations. The fracture toughness (K(Ic)), impact strength and the dynamic thermomechanical properties (T(g), E´, E´´, tanδ) of a series of PMMA-ND nanocomposites with different amounts of ND were evaluated. The fracture toughness increased as the ND percentage increased...

BACKGROUND/AIM Fracture toughness determines functional crown strenght and prevents damages on ceramics during mastication. There is a lack of relevant literature data about fracture toughness of crowns made by feather-edge preparation. Mechanical testing of ceramic samples is supposed to show if feather-edge tooth preparation is a successful method for making ceramic crowns without any risk of...

&bstracL Planar impact experiments were employed to induce dynamic tensile failure in Bedford limestone. Rock discs were impacted with aluminum and polymethyl methacralate (PMMA) flyer plates at velocities of 10 to 25 m/s. Tensile stress magnitudes and duration were chosen so as to induce a range of microcrack growth insufficient to cause complete spalling of the samples. Ultrasonic Pand S-wave...

We present a borehole failure model which is based on fracture mechanics and layer buckling theories and compare its prediction with experimental data. The model assumes that the main mechanism of borehole collapse takes place in the form of layers buckling near the borehole surface. The model introduces a combination of fracture mechanics parameters with dimension of length that scale the size...

statement of problem: tooth-coloured restorative materials are brittle with the major shortcomings of sensitivity to flaws and defects. although various mechanical properties of resin composites have been studied, no fracture toughness test data for nano-hybrid composites under acidic condition for a long period of time has been published. objectives: to compare the fracture toughness (k ic ) o...

Carving rock by indenting sharp objects into the surface under an impact force has been a favored method of fragmentation for millenia . However, as rock gets harder the lifetime of these sharp tools becomes short and, in a compromise hardened bits of rounder contour have become more common, particularly when driven by mechanical power. To better understand the behavior of these newer generatio...

changes in moisture content and temperature can perturb both stiffness and strength and as such the impact resistance of composite structures. in this paper, the pre-notched basalt fibre reinforced epoxy (bfre) composite specimens are studied under charpy impact loads in order to investigate the changes in impact energy absorption (fracture toughness) with different kinds of aging conditions. t...

An analysis is presented for transient response of a mode-III interfacial crack propagating between two dissimilar piezoelectric half spaces. The dynamic fracture toughness of a piezoelectric interface is examined, which is a central issue related to the interface strength of multi-layered sensors and ferroelectric thin film devices. For the mode-III crack propagation in piezoelectric materials...

The proportional relationships between the Charpy absorbed energy (CVN) and the KIC values have been established for a wide variety of steels. Several formulae have been proposed that predict KIC from CVN. The purpose of this study is to investigate, by means of compact testing fracture toughness specimens, the effective role of microstructure for estimation of the fractur...

Introduction: The fracture mechanisms of bone tissue have been described as a damage accumulation process, which starts with the initiation and propagation of microcracks. Knowledge of crack initiation and propagation at tissue level (tissue fracture toughness) is critical to understand and prevent bone fractures. Tissue fracture toughness could provide valuable information for defining bone qu...